Kibisan® PN-127 L150 General Purpose Grade High Flowability
KIBISAN PN-127 L150 is a high-performance, transparent blue SAN resin designed for injection molding. With excellent heat resistance, mechanical strength, and dimensional stability, it’s ideal for precision parts in electronics, appliances, and industrial applications.
- Application: External pen tubing, transparent parts for electrical and electronic products, fan blades
- Character: Transparent blue, heat resistant grade
Key technical data (ISO)
- Melt Flow Index: 17 ml/10 min (220°C, 10 kg)
- Heat Deflection Temp (Annealed): 101°C (1.8 MPa)
- Tensile Strength: 74 MPa
- Flexural Modulus: 3.3 GPa
- Mold Shrinkage: 0.2–0.7%
- Flammability Rating (UL94): HB (1.5mm)
Applications
- External Pen Tubing: Transparent, durable, and precise for smooth functionality.
- Transparent Electrical/Electronic Parts: Heat-resistant and dimensionally stable for housings and covers.
- Fan Blades: High mechanical strength and rigidity for long-lasting performance.
Kibisan® PN-127 L150 Datasheet
| General SAN KIBISAN® PN-127_L150 Product Description: Injection molding | ||||
| Properties | ISO Test Method | Test Condition | Unit | PN-127_L150 |
| Melt Flow Index | 1133 | 220℃×10KG | ml/10 min | 17 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.06 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 74 |
| 50 mm/min, break | MPa | 74 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 3 |
| Flexural Strength | 178 | 2 mm/min | MPa | 105 |
| Flexural Modulus | 2 mm/min | GPa | 3.3 | |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 3 |
| -30℃, Notched | KJ/m2 | – | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 2 |
| -30℃, Notched | KJ/m2 | – | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 105 |
| 50℃/hr;5KG | ℃ | 104 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 90 |
| 1.8MPa, annealed | ℃ | 101 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 3.6~3.8*10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.2~0.7 |
| Symbol | 1043 | – | – | >SAN< |
| March 11, 2024 Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test | ||||
Kibisan® PN-127 L150 UL Product iQ
| KIBISAN® PN-127 | UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets |
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746A |
| (1.5 mm) | ||
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746A |
| (1.5 mm) | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | |
| High Voltage, Low Current Arc Resistance | PLC 6 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
Related Kibisan® SAN (aS) Plastics
Chimei Kibisan® PN-137H SAN
Chimei Kibisan® PN-127 L150FG
Chimei Kibisan® PN-127 L200
Chimei Kibisan® PN-127 L150
Chimei Kibisan® PN-117H L150FG
Chimei Kibisan® PN-117C
Chimei Kibisan® PN-117 L100
Chimei Kibisan® PN-106 L150
Chimei Kibisan® PN-127H SAN
Chimei Kibisan® PN-107 L125 SAN
Chimei Kibisan® PN-117 L200 SAN
Chimei Kibisan® PN-127 L100
Chimei Kibisan® PN-107 L125FG
Advanced Manufacturing