Chimei Kibisan® PN-127 L150FG Low Residual Monomer

Chimei Kibisan® PN-127 L150FG Low Residual Monomer Grade SAN

KIBISAN® PN-127 L150FG is a food-safe, low-monomer SAN resin certified for EU 10/2011 and GB4806 compliance. Ideal for high-clarity applications like kitchen appliances and water filters, it combines durability, thermal stability, and exceptional transparency for precision injection-molded parts.

Application: Blender, Coffee machine, Water filter
Character: Low monomer residue (EU 10/2011 Certification, GB4806), Water clear

SAN Resin

Chimei KIBISAN® SAN Resin

Key technical data (ISO)

Melt Flow Index: 17 ml/10 min
Tensile Strength: 74 MPa
Flexural Strength: 105 MPa
Vicat Softening Temp: 105°C
Mold Shrinkage: 0.2–0.7%
Flammability (UL 94): HB (1.5 mm)

Download

ISO TDS Download

MSDS Download

UL Product iQ Download

Process Guide Download

Food-Safe & Low Monomer Residue

With EU 10/2011 and GB4806 certifications, PN-127 L150FG ensures safety for food-contact applications. Minimized residual monomers reduce contamination risks, making it perfect for water filters and food containers.

Crystal-Clear Durability

Boasting water-clear transparency and high tensile strength (74 MPa), this resin maintains aesthetics and structural integrity under stress. Ideal for transparent blender jars or coffee machine components requiring scratch resistance.

Heat-Resistant Performance

With a Vicat softening point of 105°C and heat distortion temperature up to 101°C, PN-127 L150FG withstands steam and high-temperature environments, ensuring longevity in appliances like coffee makers.

Applications

Blenders: Transparent, impact-resistant jars that endure daily wear.
Coffee Machines: Heat-resistant housings and steam-resistant components.
Water Filters: Food-safe, chemical-resistant parts with crystal clarity.

Chimei Kibisan PN-127 L150FG Application

Kibisan® PN-127 L150FG Datasheet

Low Residual Monomer SAN KIBISAN® PN-127_L150FG Product Description: Injection molding
Properties	ISO Test Method	Test Condition	Unit	PN-127_L150FG
Melt Flow Index	1133	220℃×10KG	ml/10 min	17
Mass Density	1183	23 ℃	g/cm3	1.06
Tensile Strength	527	50 mm/min, yield	MPa	74
Tensile Strength	527	50 mm/min, break	MPa	74
Tensile Elongation	527	50 mm/min	%	3
Flexural Strength	178	2 mm/min	MPa	105
Flexural Modulus	178	2 mm/min	GPa	3.3
Izod Impact Strength	180/1A	23℃, Notched	KJ/m2	3
Izod Impact Strength	180/1A	-30℃, Notched	KJ/m2	–
Charpy Impact Strength	179	23℃, Notched	KJ/m2	2
Charpy Impact Strength	179	-30℃, Notched	KJ/m2	–
Vicat Softening Temp.	306	50℃/hr;1KG	℃	105
Vicat Softening Temp.	306	50℃/hr;5KG	℃	104
Heat Distortion Temp.	75/A	1.8MPa, unannealed	℃	90
Heat Distortion Temp.	75/A	1.8MPa, annealed	℃	101
Coefficient of Linear Thermal Expansion	11359	–	–	3.6~3.8*10-5
Flammability	–	UL-94	–	1.5mm HB
Mold Shrinkage	294-4	–	%	0.2~0.7
Symbol	1043	–	–	>SAN<
March 11, 2024 Notes：These are typical properties only and are not to be construed as specifications. Users should confirm results by their own test

Kibisan® PN-127 L150FG UL Product iQ

KIBISAN® PN-127 L150 FG \| UL Product iQ
File Number: E56070	Yellow Card™	Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		ANSI/UL 94
1.5 mm, Color: ALL	HB
3.0 mm, Color: ALL	HB
ISO/IEC FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		IEC 60695-11-10
1.5 mm, Color: ALL	HB75
3.0 mm, Color: ALL	HB40
ELECTRICAL PROPERTIES	VALUE	TEST METHOD
Hot-wire Ignition (HWI)	PLC 4	UL 746A
(1.5 mm)
High Amp Arc Ignition (HAI)	PLC 0	UL 746A
(1.5 mm)
High Voltage Arc Tracking Rate (HVTR)	PLC 0
High Voltage, Low Current Arc Resistance	PLC 6
THERMAL PROPERTIES	VALUE	TEST METHOD
Relative Thermal Index – Electrical Strength		UL 746B
1.5 mm	50 °C
3.0 mm	50 °C
Relative Thermal Index – Mechanical Impact		UL 746B
1.5 mm	50 °C
3.0 mm	50 °C
Relative Thermal Index – Mechanical Strength		UL 746B
1.5 mm	50 °C
3.0 mm	50 °C

Chimei Kibisan® PN-127 L150FG