Chimei POLYLAC® PA-709P ABS
Plastic Granules
Polylac® PA-709P ABS Extrusion grade Pipe material
Chimei POLYLAC PA-709P is an extrusion-grade ABS resin designed for high-efficiency pipe production. With superior melt flow, impact resistance, and heat stability, it’s ideal for industrial, plumbing, and HVAC systems—delivering durability and safety compliance.
Associated Documents
ISO TDS
ASTM TDS
MSDS
UL Product iQ
Process Guide
Typical property data
Physical Properties
- Melt Flow Index: 5 ml/10 min (ISO 1133, 220℃ × 10KG)
- Mass Density: 1.04 g/cm³ (ISO 1183, 23℃)
Mechanical Properties
- Tensile Strength (Yield): 42 MPa (ISO 527, 50 mm/min)
- Tensile Strength (Break): 31 MPa (ISO 527, 50 mm/min)
- Tensile Elongation: 25% (ISO 527, 50 mm/min)
- Flexural Strength: 61 MPa (ISO 178, 2 mm/min)
- Flexural Modulus: 2 GPa (ISO 178, 2 mm/min)
- Izod Impact Strength (Notched, 23℃): 39 KJ/m² (ISO 180/1A)
- Charpy Impact Strength (Notched, 23℃): 39 KJ/m² (ISO 179)
Thermal Properties
- Vicat Softening Temperature (1KG): 106℃ (ISO 306, 50℃/hr)
- Vicat Softening Temperature (5KG): 99℃ (ISO 306, 50℃/hr)
- Heat Distortion Temperature (Annealed, 1.8MPa): 98℃ (ISO 75/A)
- Coefficient of Linear Thermal Expansion: 8.7×10−58.7 \times 10^{-5} (ISO 11359)
Flammability
Rating: HB at 1.5 mm (UL-94)
Mold Shrinkage
Shrinkage Range: 0.4–0.7% (ISO 294-4)
Features & Benefits
Optimized Melt Flow for Efficiency
POLYLAC PA-709P’s melt flow index (5 ml/10min) ensures smooth extrusion, reducing energy use and speeding up production for cost-effective pipe manufacturing.
Exceptional Impact Resistance
Boasting 39 KJ/m² Izod impact strength, this ABS resin withstands drops, collisions, and harsh environments, perfect for industrial drainage or heavy-duty piping.
Heat Resistance & Safety Compliance
With a Vicat softening point of 106°C and HB flammability rating, it ensures safe performance in high-temperature applications like hot water pipes or HVAC ducting.