Chimei Polylac® PA-765B ABS
Plastic Granules
Polylac® PA-765B Flame Retardant Medium Impact
Polylac PA-765B ABS Resin is a flame-retardant plastic raw material. Perfect for electronics (TV frames, printers), power panels, and car audio consoles and coffee machines and modems.
Download PDF
ISO TDS
ASTM TDS
MSDS
RoHS
SVHC
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index: 44 ml/10 min (ISO 1133, 220℃ × 10 kg)
- Mass Density: 1.16 g/cm³ (ISO 1183, 23℃)
Mechanical Properties
- Tensile Strength:
- 39 MPa (yield, ISO 527, 50 mm/min)
- 30 MPa (break, ISO 527, 50 mm/min)
- Tensile Elongation: 15% (ISO 527, 50 mm/min)
- Flexural Strength: 57 MPa (ISO 178, 2 mm/min)
- Flexural Modulus: 1.8 GPa (ISO 178, 2 mm/min)
- Izod Impact Strength:
- 24 kJ/m² (23℃, Notched, ISO 180/1A)
- 11 kJ/m² (-30℃, Notched, ISO 180/1A)
- Charpy Impact Strength:
- 25 kJ/m² (23℃, Notched, ISO 179)
- 11 kJ/m² (-30℃, Notched, ISO 179)
Thermal Properties
- Vicat Softening Temperature:
- 94℃ (50℃/hr, 1 kg, ISO 306)
- 80℃ (50℃/hr, 5 kg, ISO 306)
- Heat Distortion Temperature:
- 77℃ (1.8 MPa, unannealed, ISO 75/A)
- 85℃ (1.8 MPa, annealed, ISO 75/A)
- Coefficient of Linear Thermal Expansion: 8.55×10−58.55 \times 10^{-5} (ISO 11359)
Flammability
- UL-94 Ratings:
- 1.5 mm: V-2
- 2.5 mm: V-0, 5VB
- 3.0 mm: 5VA
Mold Shrinkage
- Range: 0.3–0.6% (ISO 294-4)
Process Guide
- Pre-drying Temperature/Time: 80–85°C for 2–4 hours (depending on humidity, reground resin ratio, and storage conditions).
- Barrel Temperature Profile:
- Max: 220°C, 220°C, 210°C
- Min: 190°C, 190°C, 180°C
- Mold Temperature: 40–70°C (varies with thickness, dimensions, gate, and runner system).
- Injection Pressure: 50–80%
- Holding Pressure: 20–50%
- Back Pressure: 5–10 kg/cm²
- Injection Speed: Slow to moderate fill speeds are recommended.
- Cushion Zone: Approx. 1/8 inch after injection for dimensional consistency.
Use & Applications
Displays, machine boxes, modems, power panels, power outlets, car batteries, cash register shells, printer casings, remote control, light boxes, fax machines, projectors, large-scale multifunctional peripherals, coffee machine, front and rear TV frames, DVD players, car audio consoles
Features & Benefits
Strong Flame Resistance
Polylac PA-765B meets strict UL94 ratings (1.5mm V-2 to 3.0mm 5VA), stopping fire spread in thin parts. Perfect for electronics and power panels needing safety.
Easy to Mold
With a 44 ml/10 min melt flow rate, it fills molds quickly and evenly. Reduces production time for items like printer casings or TV frames.
Tough in All Conditions
Survives -30°C to 80°C temperatures and resists impacts (24 KJ/m² at 23°C). Ideal for car batteries, coffee machines, and outdoor devices.
PA-765B Related Flame Retardant Grades
| Type | Grade No. | Manufacturer | Brand | Grade/Features | Use/Applications |
|---|---|---|---|---|---|
| Flame Retardant ABS | PA-765A | Chimei | POLYLAC® | High-flow FR; 1.5mm V-1, 2.1mm V-0 / 5VB, 2.5mm 5VA; MFI 48; Vicat 93°C; Izod 22 | Printer casings; TV frames; remote controls; coffee machines; car batteries |
| Flame Retardant ABS | PA-765 | Chimei | POLYLAC® | F.R. high flow; 1.0mm V-1, 1.5mm V-0 / 5VB, 2.5mm 5VA, 3.0mm 5VA; MFI 58; Vicat 91°C; Izod 21 | Printer casings; TV frames; modems; power outlets; remote controls; coffee machines |
| Flame Retardant ABS | PA-764B | Chimei | POLYLAC® | FR + weather resistant; 2.5mm V-0 / 5VB, 3.0mm 5VA; MFI 26; Vicat 102°C; HDT 93°C; Izod 14; elongation 15% | TV frames; printer casings; power outlets; outdoor appliance housings; car audio consoles |
← Back to Chimei Flame Retardant ABS Resin — view the full POLYLAC® FR-ABS portfolio, UL 94 ratings and processing guide.