Sabic CYCOLOY™ Resin C4210HF PC/ABS
Plastic Granules
Sabic Cycoloy C4210HF (PC/ABS) Resin
Cycoloy Resin C4210HF C4210HF is a 10% glass-reinforced PC+ABS blend. It delivers an exceptional balance of high flow for easy processing, high heat resistance for durability, and superior strength with good impact and appearance.
Associated Documents
TDS Europe
Typical property data
Physical Properties
- Mold Shrinkage (flow): 0.3 – 0.5% (SABIC method)
- Density: 1.22 g/cm³ (ISO 1183)
- Water Absorption (23°C, saturated): 0.6% (ISO 62-1)
- Moisture Absorption (23°C / 50% RH): 0.2% (ISO 62)
Mechanical Properties
- Tensile Stress (yield, 5 mm/min): 90 MPa (ISO 527)
- Tensile Modulus (1 mm/min): 4700 MPa (ISO 527)
- Flexural Stress (yield, 2 mm/min): 125 MPa (ISO 178)
- Flexural Modulus (2 mm/min): 4250 MPa (ISO 178)
- Ball Indentation Hardness: 116 MPa (ISO 2039-1)
- Hardness (Rockwell): 121 R-scale (ISO 2039-2)
Impact Properties
- Izod Impact Strength (notched, 23°C): 8 kJ/m² (ISO 180/1A)
- Izod Impact Strength (unnotched, 23°C): 20 kJ/m² (ISO 180/1U)
Thermal Properties
- Vicat Softening Temperature (Rate B/50): 134°C (ISO 306)
- HDT (0.45 MPa): 133°C (ISO 75/Be)
- HDT (1.8 MPa): 123°C (ISO 75/Ae)
- Thermal Conductivity: 0.2 W/m·°C (ISO 8302)
Electrical Properties
- Volume Resistivity: >1.E+15 Ω.cm (IEC 60093)
- Surface Resistivity (ROA): >1.E+15 Ω (IEC 60093)
Flame Characteristics
- Ball Pressure Test: Passes at 75°C ± 2°C and 125°C ± 2°C (IEC 60695-10-2)
Injection Molding Parameters
- Drying Temperature: 100 – 110°C
- Drying Time: 2 – 4 hours
- Melt Temperature: 240 – 280°C
- Mold Temperature: 50 – 80°C
Features & Benefits
Enhanced Flow for Complex Molding
The high flow rate of Cycoloy C4210HF PC+ABS fills intricate molds effortlessly, reducing cycle times and minimizing defects for higher productivity and lower part costs.
Withstands High-Temperature Environments
With a Heat Deflection Temperature of 123°C at 1.8 MPa, this material maintains its structural integrity in demanding applications, ensuring reliability and long-term performance.
Superior Strength and Rigidity
The 10% glass reinforcement provides excellent stiffness and strength, allowing for the design of thin-walled yet durable components that resist deformation under load.
Use & Applications
- Automotive Interior & Exterior Parts
- Electrical Enclosures & Housings
- Consumer Electronics Housings
- Industrial Components