FCFC Formosa TAIRILAC® AE8000 ABS Resin
TAIRILAC® AE8000 ABS Resin Extrusion Grade
Tairilac AE8000 is an extrusion-grade ABS resin engineered for superior impact resistance and rigidity. Ideal for high-stress industrial applications, it delivers exceptional processability, durability, and dimensional stability. Perfect for demanding extrusion products like safety gear, pipes, and structural components.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index: 4.5 g/10 min (ISO 1133, 220℃ × 10kg)
- Specific Gravity: 1.04 (ISO 1183, 23℃/23℃)
Mechanical Properties
- Tensile Strength: 42 MPa (ISO 527, 23℃, 50mm/min)
- Flexural Strength: 51 MPa (ISO 178, 23℃, 2mm/min)
- Flexural Modulus: 1500 MPa (ISO 178, 23℃, 2mm/min)
- Rockwell Hardness: R-103 (ISO 2039-2, 23℃)
Impact Properties
- Charpy Impact Strength: 47 kJ/m² (ISO 179, 23℃, 4mm thickness, Notched)
Thermal Properties
- Vicat Softening Point: 94℃ (ISO 306, Annealed, 50N, 50℃/h)
- Heat Deflection Temperature: 92℃ (ISO 75/A, Annealed, 1.8MPa, 4mm thickness, 120℃/h)
Flame Characteristics
- Combustibility: UL-94 HB (File No. E162823, 1.6 mm thickness)
Injection Molding
- Molding Shrinkage: 0.4%–0.7% (ISO 2577, 3.2mm thickness)
Features & Benefits
Optimized for Extrusion Molding
AE8000 processes smoothly at 180–230°C, enabling efficient production of complex profiles with minimal warping. Reduces downtime and energy costs.
Super High Impact Strength
With 47 kJ/m² Charpy impact resistance (ISO 179), it withstands heavy impacts—ideal for crash helmets and protective gear. Ensures end-product safety.
High Rigidity & Stability
Flexural modulus of 1,500 MPa (ISO 178) maintains shape under load. Perfect for load-bearing pipes and shoe heels needing long-term structural integrity.
Use & Applications