FCFC Formosa TAIRILAC® AE8700 ABS Resin
TAIRILAC® AE8700 ABS Resin Extrusion Grade
Tairilac® AE8700 is an extrusion-grade ABS resin engineered for super high impact resistance and exceptional rigidity. Ideal for demanding industrial profiles, it delivers unmatched dimensional stability and processability in extrusion molding.
Typical property data
Physical Properties
- Melt Flow Index (MFI): 3.5 g/10 min (ISO 1133, 220°C × 10 kg)
- Specific Gravity: 1.04 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 46 MPa (ISO 527, 23°C, 50 mm/min)
- Flexural Strength: 69 MPa (ISO 178, 23°C, 2 mm/min)
- Flexural Modulus: 2300 MPa (ISO 178, 23°C, 2 mm/min)
- Rockwell Hardness: R-109 (R-scale, ISO 2039-2, 23°C)
Impact Properties
- Charpy Impact Strength: 40 kJ/m² (ISO 179, 23°C, 4 mm thick, Notched)
Thermal Properties
- Vicat Softening Point: 95°C (ISO 306, Annealed, 50 N, 50°C/h)
- Heat Deflection Temperature (HDT): 87°C (ISO 75/A, Annealed, 1.8 MPa, 4 mm thick, 120°C/h)
Injection Molding
- Molding Shrinkage: 0.4–0.7% (ISO 2577, 3.2 mm)
Features & Benefits
Extrusion-Optimized Processability
With a balanced melt flow (3.5 g/10 min), AE8700 ensures smooth, efficient extrusion – reducing energy waste and production downtime for pipes and profiles.
Impact Resistance for Safety
Unmatched Charpy impact strength (40 kJ/m²) absorbs high-force impacts, ideal for crash helmets or protective gear that must withstand harsh conditions.
Rigidity Under Pressure
High flexural modulus (2300 MPa) prevents warping in structural parts like shoe heels or load-bearing components, ensuring long-term durability.
Use & Applications