FCFC Formosa TAIRILAC® AF3530 ABS Resin
Plastic Granules
TAIRILAC® AF3530 ABS Resin High Flow Grade
Tairilac® AF3530 is high-flow, high-impact ABS resin. Thie AF3530 plastic material delivers exceptional processability, durability, and chemical resistance—ideal for complex, high-volume injection molding.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Specific Gravity: 1.04 (ISO 1183, 23℃)
Mechanical Properties
- Tensile Strength: 40 MPa (ISO 527, 23℃, 50 mm/min)
- Flexural Strength: 52 MPa (ISO 178, 23℃, 2 mm/min)
- Flexural Modulus: 1600 MPa (ISO 178, 23℃, 2 mm/min)
- Rockwell Hardness: R-105 (ISO 2039-2, 23℃)
Impact Properties
- Charpy Impact Strength (Notched): 30 kJ/m² (ISO 179, 23℃, 4mm thickness)
Thermal Properties
- Vicat Softening Point: 93℃ (ISO 306, Annealed, 50N, 50℃/h)
- Heat Deflection Temperature (HDT): 91℃ (ISO 75/A, Annealed, 1.8 MPa, 4mm thickness, 120℃/h)
Flame Characteristics
- Combustibility: UL-94 HB (Thickness: 0.8–3 mm, UL Certification File No. E162823)
Injection Molding
- Melt Flow Index: 3 g/10 min (ISO 1133, 200℃, 5kg)
- Melt Flow Index: 27 g/10 min (ISO 1133, 220℃, 10kg)
- Molding Shrinkage: 0.4%–0.7% (ISO 2577, 3.2mm)
Features & Benefits
Superior Flow Efficiency
With an MFI of 27 g/10 min (220°C/10kg), AF3530 fills intricate molds effortlessly, reducing cycle times and minimizing warping—saving time and costs.
Exceptional Impact Strength
30 kJ/m² Charpy impact resistance (ISO 179) ensures parts withstand drops, impacts, and stress—perfect for durable consumer goods and automotive components.
Reliable Chemical Resistance
It resists oils, cleaners, and solvents, maintaining integrity in harsh environments like automotive interiors or industrial equipment.
Use & Applications