FCFC Formosa TAIRILAC® AF3535 ABS Resin
Plastic Granules
TAIRILAC® AF3535 ABS Resin High Flow Grade
Tairilac® AF3535 is a high-flow, high-impact ABS resin. Its exceptional melt fluidity fills complex molds effortlessly, while robust impact strength ensures durability in industrial and consumer products. Ideal for large, thin-walled components requiring precision and resilience.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index:
- 4.2 g/10 min (ISO 1133, 200℃ × 5 kg)
- 40 g/10 min (ISO 1133, 220℃ × 10 kg)
- Specific Gravity: 1.04 (ISO 1183, 23℃/23℃)
Mechanical Properties
- Tensile Strength: 42 MPa (ISO 527, 23℃, 50 mm/min)
- Flexural Strength: 56 MPa (ISO 178, 23℃, 2 mm/min)
- Flexural Modulus: 1700 MPa (ISO 178, 23℃, 2 mm/min)
- Rockwell Hardness: R-105 (ISO 2039-2, 23℃)
Impact Properties
- Charpy Impact Strength: 26 kJ/m² (ISO 179, 23℃, 4 mm thickness, Notched)
Thermal Properties
- Vicat Softening Point: 93℃ (ISO 306, Annealed, 50N, 50℃/h)
- Heat Deflection Temperature (HDT): 92℃ (ISO 75/A, Annealed, 1.8 MPa, 4 mm thickness, 120℃/h)
Flame Characteristics
- Combustibility: UL-94 HB for 0.8–1.7 mm thickness (File No. E162823)
Injection Molding
- Molding Shrinkage: 0.4–0.7% (ISO 2577, 3.2 mm)
Features & Benefits
Effortless Mold Filling
With a melt flow index of 40 g/10min (220°C), Tairilac ABS AF3535 reduces cycle times and energy costs, enabling flawless production of intricate geometries without sink marks.
Impact-Resistant Durability
It boasts 26 kJ/m² Charpy impact strength (ISO 179), making it perfect for parts subjected to drops or stress, like outdoor equipment or children’s toys.
Reliable Thermal Stability
It features a 92°C heat deflection temperature (ISO 75/A), ensuring dimensional integrity in warm environments (e.g., automotive interiors or electronics housings).
Use & Applications