FCFC Formosa TAIRILAC® AF3560 ABS Resin
TAIRILAC® AF3560 ABS Resin High Flow Grade
Tairilac ABS AF3560 is a high-flow, high-impact ABS resin engineered for complex, thick-walled applications. Its exceptional melt fluidity reduces cycle times, while robust impact strength ensures durability in demanding environments. Ideal for injection molding across consumer and industrial sectors.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index:
- 200°C × 5kg: 5.2 g/10 min (ISO 1133)
- 220°C × 10kg: 53 g/10 min (ISO 1133)
- Rockwell Hardness: R-109 (ISO 2039-2, 23°C)
- Molding Shrinkage: 0.4 ~ 0.7% (ISO 2577, 3.2mm)
Mechanical Properties
- Tensile Strength: 43 MPa (ISO 527, 23°C, 50mm/min)
- Flexural Strength: 58 MPa (ISO 178, 23°C, 2mm/min)
- Flexural Modulus: 1700 MPa (ISO 178, 23°C, 2mm/min)
Impact Properties
- Charpy Impact Strength: 14 kJ/m² (ISO 179, Notched, 23°C, 4mm thick)
Thermal Properties
- Vicat Softening Point: 93°C (ISO 306, Annealed, 50N, 50°C/h)
- Heat Deflection Temperature: 91°C (ISO 75/A, Annealed, 1.8MPa, 4mm thick, 120°C/h)
Flame Characteristics
- Combustibility: HB (UL-94, 1.5 ~ 3mm, File No. E162823)
Injection Molding
- Features: High flow, High impact.
Features & Benefits
Superior Flowability
With an ISO 1133 MFI of 53 g/10 min (220°C/10kg), Tairilac AF3560 fills intricate molds effortlessly, reducing injection pressure and minimizing sink marks. Benefit: Faster production and lower energy costs.
High Impact Resistance
It delivers 14 kJ/m² (ISO 179, notched) Charpy impact strength, preventing cracks in high-stress parts. Benefit: Enhanced product longevity for rugged applications.
Easy Processing
Low pre-drying needs (70–80°C × 2–3 hrs) and consistent mold shrinkage (0.4–0.7%). Benefit: Simplified workflow and reduced scrap rates.
Use & Applications