FCFC Formosa TAIRILAC® AG100H ABS Resin
Plastic Granules
TAIRILAC® AG100H ABS Resin General Purpose Grade
Tairilac® AG100H is a super high-impact ABS resin. Its exceptional toughness and easy processability make it ideal for parts requiring durability under stress. Trusted by manufacturers worldwide, this versatile material delivers reliability without compromising performance.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index (MFI): 8 g/10 min (ISO 1133, 220℃ × 10 kg)
- Specific Gravity: 1.04 (ISO 1183, 23℃)
Mechanical Properties
- Tensile Strength: 38 MPa (ISO 527, 23℃, 50 mm/min)
- Flexural Strength: 55 MPa (ISO 178, 23℃, 2 mm/min)
- Flexural Modulus: 1800 MPa (ISO 178, 23℃, 2 mm/min)
- Rockwell Hardness: R-95 (ISO 2039-2, 23℃)
Impact Properties
- Charpy Impact Strength: 40 kJ/m² (ISO 179, 23℃, 4 mm thick, Notched)
Flame Characteristics
- Combustibility: HB (UL-94, 1.5–3 mm)
Thermal Properties
- Vicat Softening Point: 95℃ (ISO 306, Annealed, 50N, 50℃/h)
- Heat Deflection Temperature (HDT): 87℃ (ISO 75/A, Annealed, 1.8 MPa, 4 mm thick, 120℃/h)
Features & Benefits
Superior Impact Resistance
Tairilac ABS AG100H excels in absorbing shocks, reducing part failures in high-stress environments. Ideal for safety gear and protective equipment where durability is non-negotiable.
Easy Processing & Stability
With straightforward pre-drying (70–80°C, 2–3 hrs) and broad screw temperature range (190–230°C), it minimizes production delays and ensures consistent molding quality.
Safety-Compliant Formulation
HB-rated flammability (UL 94) and low toxicity (GHS non-hazardous) meet strict industrial safety standards, reducing workplace risks and regulatory hurdles.