FCFC Formosa TAIRILAC® AG10AP ABS Resin
Plastic Granules
TAIRILAC® AG10AP ABS Resin Extrusion Grade
Tairilac® AG10AP ABS Resin is an extrusion-grade polymer engineered for super-high impact resistance and exceptional rigidity. Perfect for demanding industrial applications, it ensures durability and ease of processing while maintaining dimensional stability.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index: 4 g/10 min (ISO 1133, 220℃ × 10 kg)
- Specific Gravity: 1.04 (ISO 1183, 23℃/23℃)
Mechanical Properties
- Tensile Strength: 37 MPa (ISO 527, 23℃, 50 mm/min)
- Flexural Strength: 46 MPa (ISO 178, 23℃, 2 mm/min)
- Flexural Modulus: 1500 MPa (ISO 178, 23℃, 2 mm/min)
- Rockwell Hardness (R-scale): R-93 (ISO 2039-2, 23℃)
Impact Properties
- Charpy Impact Strength: 50 kJ/m² (ISO 179, 23℃, 4 mm thickness, Notched)
Thermal Properties
- Vicat Softening Point: 91°C (ISO 306, Annealed, 50N, 50℃/h)
- Heat Deflection Temperature: 92°C (ISO 75/A, Annealed, 1.8 MPa, 4 mm thickness, 120℃/h)
Flame Characteristics
- Combustibility: HB at 1.6 mm (UL-94, File No. E162823)
Injection Molding
- Molding Shrinkage: 0.4 ~ 0.7% (ISO 2577, 3.2 mm)
Features & Benefits
Super-High Impact Resistance
With a Charpy impact strength of 50 kJ/m², Tairilac AG10AP withstands heavy shocks—ideal for safety gear like crash helmets or industrial components prone to stress fractures.
Superior Rigidity & Stability
A flexural modulus of 1,500 MPa prevents deformation under load, ensuring long-lasting structural integrity for pipes, profiles, and load-bearing parts.
Optimized Extrusion Processing
Pre-drying (70–80°C, 2–3 hrs) and balanced melt flow (4 g/10 min) enable smooth, efficient production—reducing waste and energy costs.
Use & Applications