FCFC Formosa TAIRILAC® AG10NP ABS Resin
Plastic Granules
TAIRILAC® AG10NP ABS Resin Extrusion Grade
TAIRILAC® AG10NP ABS Resin is FCFC’s trusted extrusion-grade solution, engineered for super-high impact resistance and exceptional rigidity. Ideal for demanding applications like protective gear and industrial profiles, it delivers reliable performance with easy processing.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index: 5.5 g/10 min (ISO 1133, 220℃ × 10kg)
- Specific Gravity: 1.04 (ISO 1183, 23℃/23℃)
Mechanical Properties
- Tensile Strength: 42 MPa (ISO 527, 23℃, 50mm/min)
- Flexural Strength: 58 MPa (ISO 178, 23℃, 2mm/min)
- Flexural Modulus: 1900 MPa (ISO 178, 23℃, 2mm/min)
- Rockwell Hardness (R-scale): R-102 (ISO 2039-2, 23℃)
Impact Properties
- Charpy Impact Strength: 45 kJ/m² (ISO 179, 23℃, Notched, 4mm thick)
Thermal Properties
- Vicat Softening Point: 94°C (ISO 306, Annealed, 50N, 50℃/h)
- Heat Deflection Temperature: 93°C (ISO 75/A, Annealed, 1.8 MPa, 4mm thick, 120℃/h)
Flame Characteristics
- Combustibility: UL-94 HB (1.6 ~ 1.76 mm, File No. E162823)
Injection Molding
- Molding Shrinkage: 0.4–0.7% (ISO 2577, 3.2mm)
Features & Benefits
Extreme Impact Protection
With 45 kJ/m² Charpy impact strength (ISO 179), AG10NP absorbs sudden shocks without cracking – perfect for crash helmets or safety equipment exposed to drops or collisions.
Structural Rigidity Assurance
A high flexural modulus (1,900 MPa, ISO 178) ensures dimensional stability under load, preventing warping in pipes, automotive trims, or load-bearing components.
Optimized Extrusion Efficiency
It pre-dries quickly (70–80°C/2–3 hrs) and processes smoothly at 180–230°C screw temps, reducing energy use and production downtime for profiles or sheets.
Use & Applications