FCFC Formosa TAIRILAC® AG12A0 ABS Resin
Plastic Granules
TAIRILAC® AG12A0 ABS Resin General Purpose Grade
Tairilac AG12A0 is a super high-impact ABS resin engineered for toughness and process efficiency. Ideal for injection molding and extrusion in demanding industrial applications, combining durability with safety compliance.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index:
- 1.6 g/10 min (ISO 1133, 200℃ × 5 kg)
- 19 g/10 min (ISO 1133, 220℃ × 10 kg)
- Specific Gravity: 1.04 (ISO 1183, 23℃/23℃)
Mechanical Properties
- Tensile Strength: 44 MPa (ISO 527, 23℃, 50 mm/min)
- Flexural Strength: 66 MPa (ISO 178, 23℃, 2 mm/min)
- Flexural Modulus: 2300 MPa (ISO 178, 23℃, 2 mm/min)
- Rockwell Hardness: R-105 (ISO 2039-2, 23℃)
Impact Properties
- Charpy Impact Strength (Notched): 30 kJ/m² (ISO 179, 23℃, 4 mm thickness)
Thermal Properties
- Vicat Softening Point: 93℃ (ISO 306, annealed, 50N, 50℃/h)
Flame Characteristics
- Combustibility: UL-94 HB (Thickness range: 1.5–3 mm, File No. E162823)
Features & Benefits
Extreme Impact Resistance
Charpy impact strength of 30 kJ/m² ensures reliability in high-stress environments, reducing part failures and replacements.
Optimized Processing
Low pre-drying (70–80°C, 2–3 hrs) and versatile molding temps (190–230°C) cut energy costs and cycle times.
Safety-Certified
UL94 HB flammability rating and RTI 60°C electrical safety meet strict standards without additives.
Use & Applications