FCFC Formosa TAIRILAC® AG15A3 ABS Resin
Plastic Granules
TAIRILAC® AG15A3 ABS Resin General Purpose Grade
TAIRILAC AG15A3 ABS resin delivers high-gloss finishes and reliable medium-impact strength for industrial applications. This versatile thermoplastic combines aesthetic appeal with functional durability, making it ideal for injection-molded consumer goods and electronics.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index:
- 2.2 g/10 min (ISO 1133, at 200℃, 5 kg)
- 22 g/10 min (ISO 1133, at 220℃, 10 kg)
- Specific Gravity: 1.05 (ISO 1183, at 23℃/23℃)
Mechanical Properties
- Tensile Strength: 41 MPa (ISO 527, at 23℃, 50 mm/min)
- Flexural Strength: 60 MPa (ISO 178, at 23℃, 2 mm/min)
- Flexural Modulus: 2400 MPa (ISO 178, at 23℃, 2 mm/min)
Impact Properties
- Charpy Impact Strength (Notched): 26 kJ/m² (ISO 179, at 23℃, 4 mm thickness)
Thermal Properties
- Vicat Softening Point: 94℃ (ISO 306, Annealed, 50 N, 50℃/h)
- Heat Deflection Temperature (HDT): 90℃ (ISO 75/A, Annealed, 1.8 MPa, 4 mm thickness, 120℃/h)
Injection Molding
- Molding Shrinkage: 0.4% ~ 0.7% (ISO 2577, at 3.2 mm)
Flame Characteristics
- Combustibility: HB for thickness 1.0–1.65 mm (UL-94, File No. E162823)
Featurtes & Benefits
High-Gloss Aesthetic Finish
AG15A3 superior surface shine eliminates secondary painting, reducing costs for consumer products like phone housings or stereo casings while enhancing visual appeal.
Balanced Impact Resistance
With 26 kJ/m² Charpy impact strength (ISO 179), it withstands drops and stress—perfect for toys, suitcases, and clock housings needing everyday durability.
Easy Processing & Stability
Pre-dries quickly (70–80°C/2–3 hrs) and molds smoothly at 190–230°C, minimizing warpage and scrap rates for efficient high-volume production.
Use & Applications