FCFC Formosa TAIRILAC® AG15E1 ABS Resin
Plastic Granules
TAIRILAC® AG15E1 ABS Resin General Purpose Grade
Tairilac AG15E1 is high-gloss, high-rigidity ABS resin engineered for precision injection molding. FCFC ABS Resin delivers exceptional surface aesthetics, impact resistance, and flow properties—ideal for consumer goods demanding durability and premium finishes.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index (MFI):
- 2.4 g/10 min (200°C × 5kg, ISO 1133)
- 25 g/10 min (220°C × 10kg, ISO 1133)
- Rockwell Hardness: R-111 (23°C, ISO 2039-2)
- Molding Shrinkage: 0.4–0.7% (3.2mm, ISO 2577)
Mechanical Properties
- Tensile Strength: 46 MPa (23°C, 50mm/min, ISO 527)
- Flexural Strength: 70 MPa (23°C, 2mm/min, ISO 178)
- Flexural Modulus: 2500 MPa (23°C, 2mm/min, ISO 178)
Impact Properties
- Charpy Impact Strength: 16 kJ/m² (23°C, 4mm thickness, Notched, ISO 179)
Thermal Properties
- Vicat Softening Point: 95°C (Annealed, 50N, 50°C/h, ISO 306)
- Heat Deflection Temperature (HDT): 91°C (Annealed, 1.8MPa, 4mm thickness, 120°C/h, ISO 75/A)
Flame Characteristics
- Combustibility Rating: UL-94 HB (1.6mm thickness)
Injection Molding
- Features: High gloss, High rigidity
Featurtes & Benefits
Superior Impact Resistance
With 16 kJ/m² Charpy impact strength (ISO 179), Tairilac ABS AG15E1 withstands accidental drops and impacts, reducing breakage in consumer products.
Premium Surface Finish
High-gloss, painting-free surfaces save post-processing costs while maintaining consistent aesthetics for housings and visible components.
Excellent Flow for Complex Molds
High melt flow (25g/10min @220°C) ensures complete filling of intricate geometries, minimizing defects in thin-walled designs.
Use & Applications