FCFC Formosa TAIRILAC® AG15E3 ABS Resin
Plastic Granules
TAIRILAC® AG15E3 ABS Resin General Purpose Grade
Tairilac® AG15E3 is a high-gloss, high-rigidity ABS resin engineered for precision injection molding. Ideal for consumer goods demanding aesthetic appeal and structural integrity, it offers exceptional processability and consistent performance.
Associated Documents
ISO TDS
ASTM TDS
SDS
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index:
- 1.6 g/10 min (ISO 1133, 200°C × 5 kg)
- 18 g/10 min (ISO 1133, 220°C × 10 kg)
- Rockwell Hardness: R-111 (ISO 2039-2, 23°C)
- Molding Shrinkage: 0.4–0.7% (ISO 2577, 3.2 mm)
Mechanical Properties
- Tensile Strength: 49 MPa (ISO 527, 23°C, 50 mm/min)
- Flexural Strength: 72 MPa (ISO 178, 23°C, 2 mm/min)
- Flexural Modulus: 2500 MPa (ISO 178, 23°C, 2 mm/min)
Impact Properties
- Charpy Impact Strength: 18 kJ/m² (ISO 179, 23°C, notched, 4 mm thick)
Thermal Properties
- Vicat Softening Point: 93°C (ISO 306, Annealed, 50N, 50°C/h)
- Heat Deflection Temperature: 90°C (ISO 75/A, Annealed, 1.8 MPa, 4 mm thick, 120°C/h)
Flame Characteristics
- Combustibility: UL-94 HB (File No. E162823), 1.5–3 mm
Injection Molding
- Features: High gloss, high rigidity
Featurtes & Benefits
Effortless Processing & Stability
Pre-dry at 70–80°C for 2–3 hours, then mold at 190–230°C. Low shrinkage (0.4–0.7%) ensures dimensional accuracy for complex parts like thin-walled housings.
Superior Mechanical Strength
With 49 MPa tensile strength and 18 kJ/m² impact resistance (ISO 179), it withstands drops and stress—perfect for durable toys, luggage, and electronics casings.
Use & Applications