FCFC Formosa TAIRILOY® AC2300 PC/ABS
Plastic Granules
TAIRILOY® AC2300 PC ABS Resin General Grade
TAIRILOY AC2300 by Formosa Plastics is a versatile General Purpose Grade PC/ABS alloy ideal for metal-plated applications. It offers excellent impact resistance, high flexural strength, and heat tolerance. With a melt flow index of 9–21g/10min. UL94 HB fire rating ensures safety, while low shrinkage reduces post-molding issues. Perfect for durability and cost-effective production.
Typical property data
Physical Properties
- Specific Gravity: 1.08 (ISO 1183, 23°C)
Mechanical Properties
- Flexural Strength: 86 MPa (ISO 178, 23°C)
- Flexural Modulus: 2350 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-110 (ISO 2039-2, 23°C)
Impact Properties
- IZOD Impact Strength: 540 J/m (ISO 180, 23°C, 3.2 mm)
- Charpy Impact Strength: 40 kJ/m² (ISO 179, 23°C, 4 mm)
Thermal Properties
- Vicat Softening Point: 117°C (ISO 306, 10N)
Flame Characteristics
- Combustibility: UL-94 HB (File No. E162823, 1.5–1.65 mm)
Injection Molding
- Melt Flow Index:
- 9 g/10 min (ISO 1133, 240°C, 5 kg)
- 21 g/10 min (ISO 1133, 260°C, 5 kg)
- Molding Shrinkage: 0.4–0.6% (ISO 2577, 3.2 mm)
Features & Benefits
Superior Impact Resistance
With an Izod impact strength of 540 J/m (ISO 180), TAIRILOY AC2300 withstands harsh impacts, reducing part failures in automotive interiors or handheld devices.
Excellent Flowability
A melt flow index of 21 g/10min (260°C/5kg, ISO 1133) ensures smooth filling of complex molds, ideal for intricate casings like laptop hinges or thin-walled appliance parts.
Heat & Dimensional Stability
Vicat softening point of 117°C (ISO 306) and low shrinkage (0.4–0.6%) prevent warping, ensuring reliable performance in high-temperature environments like under-hood auto components.