FCFC Formosa TAIRILOY® AC3250 PC/ABS
TAIRILOY® AC3250 PC ABS Resin Self Extinguishing Grade
TAIRILOY AC3250 by FCFC is a flame-retardant, halogen-free PC/ABS alloy resin engineered for high-performance applications. Combining exceptional mechanical strength, UL94 V-0 compliance, and ease of processing, this FCFC PC Alloy Resin is ideal for 3C electronics, electrical components, and automotive interiors. Its balanced properties ensure durability, safety, and design flexibility for demanding industrial uses.
Associated Documents
ISO Data Sheet
ASTM Data Sheet
UL Product iQ
MSDS
Processing Data
Typical property data
Physical Properties
- Specific Gravity: 1.3 (ISO 1183, 23°C)
Mechanical Properties
- Tensile Strength: 640 MPa (ISO 527, 23°C)
- Flexural Strength: 1110 MPa (ISO 178, 23°C)
- Flexural Modulus: 41600 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-115 (ISO 2039-2, 23°C)
Impact Properties
- IZOD Impact Strength: 64 J/m (ISO 180, 23°C, 3.2mm)
- Charpy Impact Strength: 5 kJ/m² (ISO 179, 23°C, 4mm)
Thermal Properties
- Vicat Softening Point: 103°C (ISO 306, VICAT(10N))
Flame Characteristics
- Combustibility:
- UL-94: V-0 (1.2–3 mm)
- 5VA (3 mm)
- 5VB (2 mm)
- Features: Flame retardant, halogen-free
Injection Molding
- Melt Flow Index:
- 25 g/10 min (ISO 1133, 240°C × 5kg)
- 12 g/10 min (ISO 1133, 260°C × 2.16kg)
- Molding Shrinkage: 0.3–0.5% (ISO 2577, 3.2mm)
Features & Benefits
Superior Flame Retardancy
TAIRILOY AC3250 meets UL94 V-0 standards at 1.2–3 mm thickness, ensuring compliance with strict fire safety regulations. Ideal for electronics and appliances where ignition resistance is critical.
High Impact & Tensile Strength
With 64 J/m Izod impact strength and 640 MPa tensile strength, this PC/ABS resin withstands drops, vibrations, and mechanical stress, reducing part failures in devices and automotive components.
Low Shrinkage & Easy Molding
Molding shrinkage of 0.3–0.5% ensures dimensional stability, minimizing defects in thin-walled parts like laptop casings or intricate dashboard panels.
Use & applications