FCFC TAIRIPRO® B1101 PP Homopolymer
TAIRIPRO® B1101 Homopolymer PP Extrusion Grade
TAIRIPRO B1101 is a high-performance homopolymer polypropylene resin engineered for extrusion and blow molding. With exceptional melt strength and deep-drawing capabilities, it creates complex, durable parts ideal for industrial applications—delivering reliability without compromising process efficiency.
Typical property data
Physical Properties
- Melt Flow Index (MFI): 0.5 g/10 min (ISO 1133, 260°C, 2.16 kg)
- Specific Gravity: 0.9 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 35 MPa (ISO 527, 23°C, 50 mm/min)
- Tensile Elongation at Break: >200% (ISO 527, 23°C, 50 mm/min)
- Flexural Modulus: 1421 MPa (ISO 178, 23°C)
- Rockwell Hardness (R-Scale): R-102 (ISO 2039-2, 23°C)
Impact Properties
- IZOD Impact Strength: 69 kJ/m² (ISO 180, 23°C, 1/8″, Notched)
- IZOD Impact Strength: 69 kJ/m² (ISO 180, 23°C, 4 mm, Notched)
Thermal Properties
- Heat Deflection Temperature (HDT): 110°C (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thick, 120°C/h)
Features & Benefits
Excellent Melt Strength
It can ensure stable processing during deep-drawing operations, reducing tearing or thinning in complex shapes like automotive ducts or industrial containers.
Superior Impact Resistance
With 69 kJ/m² notched IZOD strength (ISO 180), it withstands physical stress, ideal for trays, pipes, and blow-molded products requiring durability.
High-Temperature Stability
It can maintain integrity at 110°C (HDT, ISO 75/A), ensuring dimensional reliability in thermoforming sheets or hot-fill packaging.