FCFC Formosa TAIRIPRO® B8001 PP Impact Copolymer
Plastic Granules
TAIRIPRO® B8001 Impact Copolymer PP Injection Molding
TAIRIPRO® PP B8001 is a high-performance polypropylene impact copolymer resin. With high impact strength even at sub-zero temperatures, excellent resistance to low-temperature brittleness, and a smooth, glossy finish, this material is ideal for blow molding extrusion and thermoforming. FDA-compliant formulation.
Associated Documents
ISO Data Sheet
ASTM Data Sheet
MSDS
Processing Data
Typical property data
Physical Properties
Specific Gravity: 0.9 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 26 MPa (ISO 527, 23°C, 50mm/min)
- Flexural Modulus: 1178 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-80 (ISO 2039-2, 23°C)
Impact Properties
IZOD Impact Strength:
- 108 kJ/m² (ISO 180, 0°F, 4mm, Notched)
- 734 kJ/m² (ISO 180, 73°F, 1/8″, Notched)
Thermal Properties
Heat Deflection Temperature (HDT): 105°C (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thickness, 120°C/hour)
Injection Molding
- Melt Flow Index (MFI): 0.3 g/10 min (ISO 1133, 230°C, 2.16kg)
- Molding Shrinkage: 1.5–1.9% (FCFC Method, 23°C)
Features & Benefits
Unmatched Impact Resistance
TAIRIPRO® PP B8001 delivers 80 kJ/m² impact strength at 23°C and 11 kJ/m² at -20°C, ensuring reliability in cold climates or high-stress scenarios.
Superior Surface Quality
The resin’s natural luster eliminates the need for post-processing, reducing costs for consumer goods like cosmetic containers or household items where aesthetics matter.
Easy Processing & Consistency
Optimized melt flow (0.3 g/10min) and low shrinkage (1.5–1.9%) ensure stable extrusion and blow molding, minimizing waste and downtime in high-volume production lines.
Use & applications