FCFC Formosa TAIRIPRO® B8001A3 PP Impact Copolymer
Plastic Granules
TAIRIPRO® B8001A3 Impact Copolymer Injection Molding
With excellent impact strength and superior resistance to low-temperature brittleness, TAIRIPRO B8001A3 ensures reliability in harsh environments. Ideal for extrusion, blow molding, and thermoforming, this TAIRIPRO PP resin delivers consistent performance for automotive, construction, and cold-chain packaging applications.
Associated Documents
ISO Data Sheet
ASTM Data Sheet
MSDS
Processing Data
Typical property data
Physical Properties
- Melt Flow Index (MFI): 0.3 g/10 min (ISO 1133, 230°C × 2.16 kg)
- Specific Gravity: 0.9 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 26 MPa (ISO 527, 23°C, 50 mm/min)
- Tensile Elongation at Break: >200% (ISO 527, 23°C, 50 mm/min)
- Flexural Modulus: 1178 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-80 (ISO 2039-2, 23°C)
Impact Properties
- IZOD Impact Strength (23°C, Notched): 80 kJ/m² (ISO 180, 1/8″)
- IZOD Impact Strength (0°F, Notched): 11 kJ/m² (ISO 180, 4 mm)
Thermal Properties
Heat Deflection Temperature (HDT): 105°C (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thick, 120°C/h)
Injection Molding
Molding Shrinkage: 1.5%–1.9% (ISO 2577)
Features & Benefits
Unmatched Impact Resistance
B8001A3’s IZOD impact strength of 80 kJ/m² (ISO 180) prevents cracks in high-stress components like automotive bumpers or industrial containers, reducing part replacement costs.
Reliable in Freezing Conditions
With 11 kJ/m² impact strength at -20°C (ISO 180), this resin maintains integrity for cold-chain packaging, outdoor equipment, and refrigeration systems, eliminating brittleness risks.
Seamless Processing Flexibility
A low melt flow index of 0.3 g/10 min (ISO 1133) allows smooth extrusion, blow molding, and thermoforming, minimizing energy use and production downtime.