FCFC TAIRIPRO® F1611 PP Homopolymer
Plastic Granules
TAIRIPRO® F1611 Homopolymer PP Resin Blown Film Grade
TAIRIPRO F1611 is a homopolymer polypropylene resin engineered with high slip and anti-block properties. This versatile material delivers exceptional processing efficiency and reliability for demanding packaging solutions, backed by ISO-certified quality. Ideal for high-performance blown film applications.
Typical property data
Physical Properties
- Melt Flow Index: 10.5 g/10 min (ISO 1133, 230°C × 2.16 kg)
- Specific Gravity: 0.9 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 35 MPa (ISO 527, 23°C, 50 mm/min)
- Tensile Elongation at Break: >200% (ISO 527, 23°C, 50 mm/min)
- Flexural Modulus: 15,000 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-100 (R-scale, ISO 2039-2, 23°C)
Impact Properties
- Izod Impact Strength: 27 kJ/m² (ISO 180, 23°C, Notched, 1/8″ and 4mm)
Thermal Properties
- Heat Deflection Temperature: 115°C (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thickness, 120°C/h)
Features & Benefits
Optimized Processing Efficiency
With an ISO 1133 melt flow rate of 10.5 g/10 min, F1611 ensures smooth extrusion and reduced energy consumption. Ideal for high-speed blown film lines.
Superior Film Performance
200% elongation at break (ISO 527) and 27 kJ/m² impact strength (ISO 180) prevent tearing during production. Reduces waste in packaging operations.
Safe & Easy Handling
Non-hazardous (GHS-exempt) and stable below 60°C. Simplifies storage and meets global safety standards.
Use & Applications