FCFC TAIRIPRO® F2011 PP Homopolymer
Plastic Granules
TAIRIPRO® F2011 Homopolymer PP Resin Film Grade
TAIRIPRO F2011 Homopolymer PP Resin is a high-performance polypropylene designed for precision film applications. Featuring middle slipping and exceptional clarity, this versatile resin delivers reliable processability and optical excellence for demanding packaging solutions. Ideal for extrusion and molding, it balances efficiency with end-product quality.
Typical property data
Physical Properties
- Melt Flow Index: 7 g/10 min (ISO 1133, 230℃, 2.16 kg)
- Specific Gravity: 0.9 – (ISO 1183, 23℃/23℃)
Mechanical Properties
- Tensile Strength: 31 MPa (ISO 527, 50 mm/min, 23℃)
- Tensile Elongation at Break: >200% (ISO 527, 50 mm/min, 23℃)
- Flexural Modulus: 1274 MPa (ISO 178, 23℃)
- Rockwell Hardness: R-100 (ISO 2039-2, 23℃)
Impact Properties
- IZOD Impact Strength: 34 kJ/m² (ISO 180, 23℃, Notched, 1/8″)
- IZOD Impact Strength: 34 kJ/m² (ISO 180, 23℃, Notched, 4 mm)
Thermal Properties
- Heat Deflection Temperature: 105℃ (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thickness, 120℃/h)
Optical Properties
- Good clarity
Injection Molding
- Features: Middle slipping
Features & Benefits
Superior Optical Clarity
TAIRIPRO® F2011 offers crystal-clear transparency, enhancing product visibility for consumer packaging like food wraps or display films – no additives needed.
Balanced Processing Ease
Its middle slipping properties reduce friction during high-speed extrusion, minimizing downtime and ensuring smooth production of thin, uniform films.
Reliable Thermal Stability
With a high melting point (140–170°C) and heat deflection temperature (105°C), it withstands rigorous processing without degrading, maintaining consistency in output.
Use & Applications