FCFC TAIRIPRO® K1023 PP Homopolymer
TAIRIPRO® K1023 Homopolymer PP injection molding grade
TAIRIPRO K1023 is a premium homopolymer polypropylene (PP) resin engineered by FORMOSA CHEMICALS & FIBRE CORPORATION (FCFC), Taiwan. With high fluidity, excellent stiffness, and superior surface luster, it delivers consistent performance for precision injection molding. Ideal for thin-walled components, consumer goods, and FDA-compliant applications.
Associated Documents
ISO Data Sheet
ASTM Data Sheet
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index: 25 g/10 min (ISO 1133, 230°C × 2.16 kg)
- Specific Gravity: 0.9 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 33 MPa (ISO 527, 23°C, 50 mm/min)
- Tensile Elongation at Break: >200% (ISO 527, 23°C, 50 mm/min)
- Flexural Modulus: 1372 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-100 (ISO 2039-2, 23°C)
Impact Properties
- IZOD Impact Strength: 25 kJ/m² (ISO 180, 23°C, Notched, 1/8″ and 4 mm)
Thermal Properties
- Heat Deflection Temperature (HDT): 110°C (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thick, 120°C/h)
Flame Characteristics
- Combustibility: HB (UL-94, File No. E162823, 1.5–3 mm)
Injection Molding
- Molding Shrinkage: 1.4–1.8% (FCFC Method, 23°C)
Features & Benefits
Exceptional Processing Efficiency
TAIRIPRO® K1023’s high melt flow index (25 g/10 min, ISO 1133) ensures rapid, uniform mold filling—reducing cycle times and energy costs for high-volume production.
Reliable Structural Integrity
Boasting a flexural modulus of 1,372 MPa (ISO 178), it provides outstanding rigidity and dimensional stability for durable parts that resist deformation under stress.
Premium Aesthetics & Safety
Delivers glossy, defect-free surfaces without post-processing. HB-rated flammability (UL 94) and USP Class VI compliance ensure safety for household, toy, and medical uses.
Use & Applications