FCFC TAIRIPRO® K1080 PP Homopolymer
TAIRIPRO® K1080 Homopolymer PP Injection Molding Grade
TAIRIPRO® K1080 is an ultra-high-fluidity homopolymer PP resin engineered for precision injection molding. With exceptional stiffness and glossy surface finishes, it solves flow challenges in complex, thin-walled designs while reducing cycle times. Ideal for demanding applications like toys and housewares.
Typical property data
Physical Properties
- Melt Flow Index (MFI): 80 g/10 min (ISO 1133, 230°C × 2.16 kg)
- Specific Gravity: 0.9 (ISO 1183, 23°C)
Mechanical Properties
- Tensile Strength: 34 MPa (ISO 527, 23°C, 50 mm/min)
- Tensile Elongation at Break: >50% (ISO 527, 23°C, 50 mm/min)
- Flexural Modulus: 1372 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-102 (ISO 2039-2, 23°C)
Impact Properties
- IZOD Impact Strength: 20 kJ/m² (ISO 180, 23°C, 1/8″, Notched)
- IZOD Impact Strength: 20 kJ/m² (ISO 180, 23°C, 4 mm, Notched)
Thermal Properties
- Heat Deflection Temperature (HDT): 110°C (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thickness, 120°C/h)
Optical Properties
- Features: Good luster
Injection Molding
- Molding Shrinkage: 1.4% ~ 1.8% (FCFC Method, 23°C)
Features & Benefits
Ultra-High Molding Fluidity
TAIRIPRO K1080 PP resin flows effortlessly (MFR 80 g/10 min) into intricate molds, enabling flawless production of thin-walled parts like toy gears—cutting energy use and cycle times by 20%.
Rigidity for Lightweight Durability
It boasts 1,372 MPa flexural modulus, ensuring parts like houseware containers resist deformation under load while using 15% less material versus standard PP resins.
Premium Aesthetic Finish
It delivers consistent, high-gloss surfaces without post-processing—perfect for visible components like appliance housings or toy shells—enhancing brand appeal.
Use & Applications