FCFC TAIRIPRO® K1525 PP Homopolymer
Plastic Granules
TAIRIPRO® K1525 Homopolymer PP injection molding grade
TAIRIPRO K1525 is a premium homopolymer polypropylene resin engineered for high-performance injection molding. Combining high fluidity, rigidity, gloss, and transparency, this tairipro k1525 pp resin ensures effortless processing and exceptional end-product aesthetics. Ideal for demanding applications where clarity and structural integrity are critical.
Associated Documents
ISO Data Sheet
ASTM Data Sheet
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index (MFI): 25 g/10 min (ISO 1133, 230℃, 2.16 kg)
- Specific Gravity: 0.9 (ISO 1183, 23℃/23℃)
Mechanical Properties
- Tensile Strength: 35 MPa (ISO 527, 23℃, 50 mm/min)
- Tensile Elongation at Break: >50% (ISO 527, 23℃, 50 mm/min)
- Flexural Modulus: 1764 MPa (ISO 178, 23℃)
- Rockwell Hardness (R-scale): R-108 (ISO 2039-2, 23℃)
Impact Properties
- IZOD Impact Strength (Notched):
- 25 kJ/m² (ISO 180, 23℃, 1/8″)
- 25 kJ/m² (ISO 180, 23℃, 4 mm)
Thermal Properties
- Heat Deflection Temperature (HDT): 125℃ (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thick, 120℃/h)
Optical Properties
- Features: Good luster, Good transparency
Flame Characteristics
- Combustibility: HB (UL-94, File No. E162823, 1.5 ~ 3 mm)
Injection Molding
- Molding Shrinkage: 1.4 ~ 1.8% (Formosa Chemicals Method, 23℃)
Features & Benefits
Superior Flow for Complex Molds
TAIRIPRO® K1525’s high melt flow index (25 g/10 min) fills intricate molds rapidly, minimizing cycle times and production costs while reducing material waste.
Exceptional Rigidity & Durability
With high stiffness (1,764 MPa flexural modulus) and impact strength, this Tairipro pp resin delivers warp-resistant parts that endure mechanical stress in harsh environments.
Premium Surface Finish
Excellent transparency and luster eliminate post-processing, creating visually appealing products like containers straight off the production line.
Use & Applications