FCFC TAIRIPRO® K2051 PP Homopolymer
Plastic Granules
TAIRIPRO® K2051 Homopolymer PP injection molding grade
TAIRIPRO® K2051 Homopolymer PP Resin delivers exceptional performance for demanding injection molding applications. Manufactured by FCFC Taiwan, this ultra-high-fluidity resin combines high stiffness, low warpage, and brilliant surface luster—ideal for precision thin-walled parts. Nucleating agents ensure dimensional stability, making it a top choice for engineers seeking efficiency and aesthetics.
Typical property data
Physical Properties
- Melt Flow Index: 50 g/10 min (ISO 1133, 230°C × 2.16 kg)
- Specific Gravity: 0.9 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 39 MPa (ISO 527, 23°C, 50 mm/min)
- Tensile Elongation at Break: >50% (ISO 527, 23°C, 50 mm/min)
- Flexural Modulus: 1960 MPa (ISO 178, 23°C)
- Rockwell Hardness: R-110 (ISO 2039-2, 23°C)
Impact Properties
IZOD Impact Strength (Notched):
- 23°C, 1/8″ specimen: 39 kJ/m² (ISO 180)
- 23°C, 4 mm specimen: 39 kJ/m² (ISO 180)
Thermal Properties
Heat Deflection Temperature: 135°C (ISO 75/A, Unannealed, 0.455 MPa, 1/4″ thick, 120°C/h)
Features & Benefits
Ultra-High Fluidity for Complex Molds
TAIRIPRO K2051 PP resin flows effortlessly into intricate molds (MFI: 50 g/10 min), reducing cycle times and enabling thinner wall designs without defects.
Superior Stiffness & Dimensional Stability
With a flexural modulus of 1,960 MPa and low shrinkage (1.4–1.8%), parts resist warping and maintain precise tolerances under stress—critical for snap-fit components.
Premium Surface Finish
Nucleating agents deliver a glossy, paint-ready finish, eliminating secondary polishing for toys, housewares, and consumer products.
Use & Applications