FCFC Formosa TAIRIREX® GP5000
Plastic Granules
TAIRIREX® GP5000 GPPS Resin General Grade
With excellent processability and consistent performance, TAIRIREX GP5000 PP plastic material is ideal for producing lightweight, rigid components in high-volume manufacturing. Its low residual monomer content ensures safety for diverse applications, from packaging to consumer goods.
Associated Documents
ISO Data Sheet
ASTM Data Sheet
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index: 10 g/10min (ISO 1133, 200℃ × 5 kg)
- Residual Monomer: Max 700 ppm
Mechanical Properties
- Tensile Strength: 42 MPa (ISO 527, 23℃, 20 mm/min)
- Tensile Modulus: 3400 MPa (ISO 527, 23℃, 1 mm/min)
- Tensile Elongation: 3% (ISO 527, 23℃, 20 mm/min)
- Flexural Strength: 72 MPa (ISO 178, 23℃, 2 mm/min)
- Flexural Modulus: 3400 MPa (ISO 178, 23℃, 2 mm/min)
Impact Properties
- IZOD Impact Strength: 1.6 kJ/m² (ISO 180, 23℃, 4 mm, Unnotched)
- Charpy Impact Strength: 8.7 kJ/m² (ISO 179, 23℃, 4 mm, Unnotched)
Thermal Properties
- Vicat Softening Point: 94℃ (ISO 306, Annealed 80℃ × 2 hr, 4 mm, 10 N, 50℃/h)
- Heat Deflection Temperature: 89℃ (ISO 75/A, Annealed 80℃ × 2 hr, 120℃/h, 1.8 MPa, 4 mm)
Flame Characteristics
- Combustibility: UL-94 HB, 1.5 ~ 1.7 mm (File No. E162823)
Injection Molding
- High flow, suitable for injection molding
Features & Benefits
Superior Flow
High melt flow (10 g/10min) ensures rapid filling of intricate molds, reducing cycle times and energy costs. Perfect for thin-walled products like disposable cutlery.
Reliable Mechanical Strength
With 42 MPa tensile strength and 72 MPa flexural strength, this GPPS resin resists deformation under stress, ensuring durability in items like cosmetic containers or electronic housings.
Thermal Stability & Safety
A Vicat softening point of 94°C and UL94 HB flammability rating provide heat resistance and fire safety, suitable for appliances and automotive interior parts.
Use & Applications