FCFC Formosa TAIRISAN® NF2200 SAN
Plastic Granules
TAIRISAN® NF2200 Injection Molding Grade
TAIRISAN NF2200 is a high-performance Styrene Acrylonitrile resin (SAN) engineered by Formosa Chemicals. Combining high heat resistance (Vicat 101°C) and excellent chemical stability, this injection-grade material excels in precision parts like fan blades and battery housings, offering durability and dimensional accuracy.
Associated Documents
ISO Data Sheet
ASTM Data Sheet
UL Product iQ
Processing Data
Typical property data
Physical Properties
- Melt Flow Index:
- 2.9 g/10 min (ISO 1133, 200°C × 5 kg)
- 29 g/10 min (ISO 1133, 220°C × 10 kg)
- Specific Gravity: 1.06 (ISO 1183, 23°C/23°C)
Mechanical Properties
- Tensile Strength: 73 MPa (ISO 527, 23°C, 50 mm/min)
- Flexural Strength: 117 MPa (ISO 178, 23°C, 2 mm/min)
- Flexural Modulus: 3600 MPa (ISO 178, 23°C, 2 mm/min)
- Rockwell Hardness: R-78 (ISO 2039-2, 23°C)
Thermal Properties
- Vicat Softening Point: 101°C (ISO 306, annealed, 50N, 50°C/h)
- Heat Deflection Temperature: 102°C (ISO 75/A, annealed, 1.8 MPa, 4 mm thickness, 120°C/h)
Flame Characteristics
- Combustibility: HB (UL-94, 1.5 mm thickness, File No. E162823)
Injection Molding
- Molding Shrinkage: 0.4% ~ 0.7% (ISO 2577, 3.2 mm)
Features & Benefits
High Flow Efficiency
Melt flow rate (29 g/10 min at 220°C) enables faster injection cycles, reducing production time and costs for high-output manufacturing.
Exceptional Thermal Stability
It retains structural integrity up to 102°C (HDT), minimizing warping in high-heat environments. Perfect for automotive components or appliances requiring consistent performance under thermal stress.
Exceptional Dimensional Stability
Its Vicat softening point of 101°C and HDT of 102°C allow stable performance in high-temperature environments, ideal for heat-resistant applications.
Use & Applications