Huasheng HS032S Polycarbonate
Plastic Granules
HS032S Polycarbonate Pellets High Viscosity Drinking Water Bucket
Huasheng HS032S is a high-viscosity polycarbonate resin for blow-molded drinking water buckets. It offers clear appearance, stable melt strength, 88% transmittance, 60 MPa tensile strength, and 145℃ Vicat softening temperature.
Associated Documents
TDS - Technical Data Sheet
Typical property data
Physical Properties
- Melt Mass-Flow Rate, MFR: 2.7 ± 0.5 g/10 min at 300℃ / 1.2 kg (GB/T 3682.1-2008)
- Density: 1200 kg/m³ (GB/T 1033.1-2008)
- Viscosity-Average Molecular Weight, Mv: 25,250–26,250 g/mol (GB/T 36214.2-2018)
Mechanical Properties
- Tensile Strength at Yield: 60 MPa (GB/T 1040.1-2018)
- Elongation at Break: 110% (GB/T 1040.1-2018)
- Flexural Strength: 95 MPa (GB/T 9341-2008)
- Izod Impact Strength: 72 kJ/m² (GB/T 1043.2-2018)
Optical Performance
- Light Transmittance: 88% at 1 mm (GB/T 2410-2008)
- b Value: 0–0.5 at 2 mm (GB/T 39822-2021)
- Yellow Index, YI: 0–1 at 2 mm (GB/T 39822-2021)
Thermal Properties
- Heat Deflection Temperature: 126℃ at 1.8 MPa (GB/T 1634.2-2019)
- Molding Shrinkage: 0.6–0.8% (GB/T 39818-2021)
- Vicat Softening Temperature: 145℃ (GB/T 1633-2000)
- Glass Transition Temperature: 147℃ (GB/T 19466.2-2004)
Flammability Rating
- Limited Oxygen Index, LOI: 27% (GB/T 2406.1-2008)
- Flame Retardant Grade: V-2 (GB/T 2408-2021)
Processing Parameters
- Processing Method: Blow molding
- Melt Mass-Flow Rate Reference: 2.7 ± 0.5 g/10 min at 300℃ / 1.2 kg (GB/T 3682.1-2008)
- Molding Shrinkage: 0.6–0.8% (GB/T 39818-2021)
Use & Applications
- Drinking water bucket