Huasheng HS152R Polycarbonate
Plastic Granules
HS152R Polycarbonate Granules Low Viscosity General
Associated Documents
TDS - Technical Data Sheet
Typical property data
Physical Properties
- Melt Mass-Flow Rate, MFR: 15 ± 2 g/10 min
Condition: 300℃ / 1.2 kg (GB/T 3682.1-2008) - Density: 1200 kg/m³ (GB/T 1033.1-2008)
- Viscosity-Average Molecular Weight, Mv: 23,500 g/mol (GB/T 36214.2-2018)
Mechanical Properties
Tensile Strength at Yield: 60 MPa (GB/T 1040.1-2018)
Elongation at Break: 110% (GB/T 1040.1-2018)
Flexural Strength: 95 MPa (GB/T 9341-2008)
Izod Impact Strength: 62 kJ/m² (GB/T 1043.2-2018)
Optical Performance
Light Transmittance: 89%
Thickness: 1 mm (GB/T 2410-2008)Color b Value: 0–0.5
Thickness: 2 mm (GB/T 39822-2021)Yellow Index, YI: 0–1
Thickness: 2 mm (GB/T 39822-2021)
Thermal Properties
Heat Deflection Temperature, HDT: 123℃
Condition: 1.8 MPa (GB/T 1634.2-2019)Molding Shrinkage: 0.6–0.8% (GB/T 39818-2021)
Vicat Softening Temperature: 144℃ (GB/T 1633-2000)
Glass Transition Temperature, Tg: 147℃
(GB/T 19466.2-2004)
Flammability Rating
Limited Oxygen Index, LOI: 27% (GB/T 2406.1-2008)
Flame Retardant Grade: V-2 (GB/T 2408-2021)
Processing Parameters
Processing Method: Extrusion molding, Injection molding
Processing Behavior: Low viscosity
Demolding Performance: Good demolding performance
Use & Applications
- General use