Invista™ HV360AHSL Nylon66
Plastic Granules
Invista™ HV360AHSL High Viscosity PA66 Resin
INVISTA™ HV360AHSL is a high-viscosity PA66 resin offering exceptional thermal stability and superior lubrication. Designed for both extrusion and injection molding, it ensures precision, durability, and efficiency across demanding applications.
Associated Documents
TDS - Data Sheet
Typical property data
Physical Properties
- Density: 1.14 g/cm³ (ISO 1183)
- Mold Shrinkage Parallel (2.0 mm): 2.0% (ISO 294-4)
- Mold Shrinkage Transverse (2.0 mm): 1.9% (ISO 294-4)
- Water Absorption (24 hours): 1.6% (ISO 62)
- Water Absorption (Equilibrium @ 50% RH): 2.7% (ISO 62)
Mechanical Properties
- Tensile Strength at Yield: 88 MPa (ISO 527)
- Elongation at Yield: 4.4% (ISO 527)
- Elongation at Break: 25% (ISO 527)
- Tensile Modulus: 3000 MPa (ISO 527)
- Flexural Modulus: 2950 MPa (ISO 178)
- Flexural Strength: 102 MPa (ISO 178)
- Notched Charpy (23°C): 5.5 kJ/m² (ISO 179)
- Notched Charpy (-30°C): 6.6 kJ/m² (ISO 179)
- Unnotched Charpy (23°C): NB kJ/m² (ISO 179)
- Unnotched Charpy (-30°C): NB kJ/m² (ISO 179)
- Notched Izod at 23°C: 4.9 kJ/m² (ISO 180)
Viscosity Properties
- Relative Viscosity (RV) in Formic Acid: 360 Nominal (ASTM D789)
- Viscosity Number (VN) at 0.5% in Formic Acid: 340 mL/g (ISO 307)
- Viscosity Number (VN) at 0.5% in Sulfuric Acid: 340 mL/g (ISO 307)
- Relative Viscosity (RV) at 1% in Sulfuric Acid: 5.2 Nominal (ASTM D789)
Thermal Properties
- Melting Temperature (10°C/min): 262°C (ISO 11357)
- HDT at 0.45 MPa: 183°C (ISO 75)
- HDT at 1.80 MPa: 61°C (ISO 75)
Flame Characteristics
- UL94 Flame Rating (0.40 mm): HB (UL 94)
- UL94 Flame Rating (0.71 mm): HB (UL 94)
- UL94 Flame Rating (1.50 mm): HB (UL 94)
- UL94 Flame Rating (3.00 mm): HB (UL 94)
Injection Molding
- Drying Temperature: 90°C
- Drying Time: 3–4 hrs
- Barrel Temperatures:
- Rear: 250–280°C
- Middle: 275–290°C
- Front: 275–290°C
- Nozzle: 275–295°C
- Processing Temperature (Melt): 280–295°C
- Mold Temperature: 50–90°C
- Back Pressure: 2–10 bar
- Vent Depth: 0.007–0.04 mm
- Cushion Range: 4–6 mm
- Suggested Moisture (Max): 0.03% wt
- Suggested Moisture (Min): 0.02% wt
- Screw Speed: 50–150 rpm
Use & Applications
for extrusion and injection molding applications.