Invista™ U4630HSL BKB01 Heat Stabilized Black Color PA66
INVISTA™ U4630HSL BKB01 is a high-performance PA66 resin engineered for durability, precision, and reliability in demanding environments. Heat-stabilized and lubricated both internally and externally, this black-colored resin ensures excellent retention of properties under high temperatures.
Associated Documents
TDS - Data Sheet
Typical property data
Physical Properties
- Density: 1.14 g/cm³ (ISO 1183)
- Mold Shrinkage (2.0 mm):
- Parallel: 1.8% (ISO 294-4)
- Transverse: 1.6% (ISO 294-4)
- Water Absorption:
- 24 hours: 1.7% (ISO 62)
- Equilibrium @ 50% RH: 2.6% (ISO 62)
Mechanical Properties
- Tensile Strength at Yield: 84 MPa (ISO 527)
- Tensile Modulus: 3150 MPa (ISO 527)
- Flexural Modulus: 2900 MPa (ISO 178)
- Flexural Strength (at 3.5% strain): 97 MPa (ISO 178)
- Notched Charpy Impact Strength:
- @ 23°C: 5.0 kJ/m² (ISO 179)
- @ -30°C: 4.2 kJ/m² (ISO 179)
- Unnotched Charpy Impact Strength:
- @ 23°C: NB (“No Break”) (ISO 179)
- @ -30°C: 180 kJ/m² (ISO 179)
Viscosity Properties
- Relative Viscosity in Formic Acid: 46 (ASTM D789)
- Viscosity Number (VN):
- @ 0.5% in Sulfuric Acid: 147 mL/g (ISO 307)
- @ 0.5% in Formic Acid: 134 mL/g (ISO 307)
Thermal Properties
- Melting Temperature (10°C/min): 262°C (ISO 11357)
- Heat Deflection Temperature (HDT):
- @ 0.45 MPa: 208°C (ISO 75)
- @ 1.80 MPa: 67°C (ISO 75)
- Coefficient of Linear Thermal Expansion (CLTE) (2.0 mm):
- Parallel @ 23 – 55°C: *0.9 10⁻⁴/°C (ISO 11359)
- Transverse @ 23 – 55°C: *0.9 10⁻⁴/°C (ISO 11359)
Electrical Properties
- Dielectric Strength (1.0 mm): 18 kV/mm (UL 746A)
- Comparative Tracking Index (CTI, 3.0 mm): 600 V (IEC 60112)
- High Voltage Arc Tracking Rate (HVTR): PLC 0 (UL 746A)
Flame Characteristics
- Flame Rating:
- 0.40 – 3.0 mm Thickness: V-2 (UL 94)
- Glow-Wire Flammability Index:
- @ 0.71 mm: 960°C (IEC 60695)
- @ 1.5 mm: 960°C (IEC 60695)
- @ 3.0 mm: 960°C (IEC 60695)
Injection Molding
- Drying Temperature: 80°C
- Drying Time: 3 – 4 hrs
- Barrel Temperatures:
- Rear: 250 – 270°C
- Middle: 270 – 290°C
- Front/Nozzle: 270 – 290°C
- Melt Temperature: 280 – 295°C
- Mold Temperature: 50 – 90°C
- Back Pressure: 5 – 30 bar
- Suggested Moisture Content (max): 0.20 wt%
- Screw Speed: 50 – 150 rpm
Use & Applications
- Automotive Sector
- Electrical and Electronics
- Industrial Machinery and Equipment
- Consumer Goods