Invista™ U4630HSL Nylon66
Plastic Granules
Invista™ U4630HSL Heat Stabilized Natural Color PA66
INVISTA™ U4630HSL is a premium heat-stabilized, lubricated PA66 resin known for its excellent performance in high-temperature applications. Engineered for durability and processability, this resin features advanced internal and external lubrication for seamless molding and long-lasting property retention.
Associated Documents
TDS - Data Sheet
Typical property data
Physical Properties
- Density: 1.14 g/cm³ (ISO 1183)
- Mold Shrinkage, 2.0 mm (parallel): 1.8% (ISO 294-4)
- Mold Shrinkage, 2.0 mm (transverse): 1.7% (ISO 294-4)
- Water Absorption (24 hours): 1.7% (ISO 62)
- Water Absorption (Equilibrium @ 50% RH): 2.6% (ISO 62)
Mechanical Properties
- Tensile Strength at Yield: 84 MPa (ISO 527)
- Elongation at Yield: 4.4% (ISO 527)
- Elongation at Break: 30% (ISO 527)
- Tensile Modulus: 3100 MPa (ISO 527)
- Flexural Strength: 94 MPa (ISO 178)
- Flexural Modulus: 2900 MPa (ISO 178)
- Notched Charpy Impact Strength at 23°C: 5.0 kJ/m² (ISO 179)
- Notched Charpy Impact Strength at -30°C: 4.2 kJ/m² (ISO 179)
Viscosity Properties
- Relative Viscosity (RV) in Formic Acid: 46 (ASTM D789)
- Viscosity Number (VN) at 0.5% in Sulfuric Acid: 147 mL/g (ISO 307)
- Viscosity Number (VN) at 0.5% in Formic Acid: 134 mL/g (ISO 307)
Thermal Properties
- Melting Temperature: 261°C (ISO 11357)
- Heat Deflection Temperature (HDT), 0.45 MPa: 185°C (ISO 75)
- Heat Deflection Temperature (HDT), 1.80 MPa: 62°C (ISO 75)
- Coefficient of Linear Thermal Expansion (CLTE), Parallel: 0.9 × 10⁻⁴/°C (ISO 11359)
- Coefficient of Linear Thermal Expansion (CLTE), Transverse: 0.9 × 10⁻⁴/°C (ISO 11359)
Electrical Properties
- Dielectric Strength (1.0 mm): 18 kV/mm (UL 746A)
- Comparative Tracking Index (CTI), 3.0 mm: 600 volts (IEC 60112)
Flame Characteristics
- Flame Rating (UL 94, various thicknesses): V-2
- At 0.40 mm, 0.71 mm, 1.5 mm, and 3.0 mm
- Glow-Wire Flammability Test (IEC 60695): 960°C
- At 0.71 mm, 1.5 mm, and 3.0 mm
Injection Molding
- Drying Temperature: 80°C
- Drying Time: 3 – 4 hours
- Barrel Temperatures: 250-290°C (Rear, Middle, Front)
- Nozzle Temperature: 270-290°C
- Melt Temperature: 280-295°C
- Mold Temperature: 50-90°C
- Back Pressure: 2-10 bar
- Vent Depth: 0.007-0.04 mm
- Screw Speed: 75-180 rpm
Use & Applications
- Automotive Industry
- Electronics and Electrical Sector
- Industrial Machinery & Mechanical Components
- Consumer Goods
- Fluid-Handling Equipment