LG Chem ABS AF365HB
Plastic Granules
LG ABS AF365HB Flame Retardant Grade
LG ABS AF365HB is a flame-retardant ABS resin offering V-0 rating at 2.0mm, high thermal resistance, excellent impact strength, and a bright white, high-gloss finish ideal for demanding applications like battery components.
Typical property data
Physical Properties
- Melt Flow Index: 25 g/10min (220°C, 10kg, ASTM D1238)
Mechanical Properties
- Tensile Strength at Yield: 41 MPa (23°C, 50mm/min, 3.2mm, ASTM D638)
- Flexural Strength: 61 MPa (23°C, 10mm/min, 6.4mm, ASTM D790)
- Flexural Modulus: 2150 MPa (23°C, 10mm/min, 6.4mm, ASTM D790)
- Izod Impact Strength (Notched): 33 J/m (6.4mm, 23°C, ASTM D256)
- Rockwell Hardness: 100, R-Scale (ASTM D785)
Impact Properties
- Izod Impact Strength (Notched): 33 J/m (6.4mm, 23°C, ASTM D256)
Thermal Properties
- Heat Deflection Temperature (HDT): 83°C (Edgewise, 1.82MPa, 6.4mm, Unannealed, ASTM D648)
Flame Characteristics
- Flame Retardancy: 2.0mm V-0 (UL 94 standard)
Injection Molding
- Drying Temperature: 80–90°C
- Drying Time: 3–4 hours
- Injection Temperature: 200–230°C
- Mold Temperature: 40–60°C
- Screw Speed: 30–60 rpm
Features & Benefits
Superior Flame Retardant Performance
This ABS resin achieves a UL94 V-0 rating at just 2.0mm, enhancing product safety and helping you meet stringent international safety standards for electronics and enclosures.
Excellent Thermal & Impact Stability
It combines high heat resistance with robust impact strength, ensuring durable, reliable performance that withstands both physical stress and elevated operating temperatures.
Exceptional Aesthetics and Processability
The material offers a bright white base, high gloss, and excellent colorability for a premium look, alongside easy injection molding and post-processing like painting or hot stamping.
Use & Applications
- Battery Housings and Components for consumer electronics, power tools, and energy storage systems.