LG Chem ABS AF367H
Plastic Granules
LG ABS AF367H Flame Retardant Grade
LG Chem’s ABS AF367H is a high-performance, flame-retardant ABS resin designed for injection molding. It offers exceptional thermal stability and a V-0 fire resistance rating at 2.5mm, making it a reliable and safe choice for demanding electronic and healthcare applications.
Typical property data
Physical Properties
- Melt Flow Index: 30 g/10min, tested at 220℃, 10kg (ASTM D1238)
Mechanical Properties
- Tensile Strength (at Yield): 43 MPa, tested at 23℃, 50mm/min, 3.2mm (ASTM D638)
- Flexural Strength: 65 MPa, tested at 23℃, 10mm/min, 6.4mm (ASTM D790)
- Flexural Modulus: 2300 MPa, tested at 23℃, 10mm/min, 6.4mm (ASTM D790)
- Izod Impact Strength (Notched): 20 J/m, tested at 23℃, 6.4mm (ASTM D256)
- Rockwell Hardness: R-Scale: 105 (ASTM D785)
Thermal Properties
- Heat Deflection Temperature: 85℃, tested edgewise at 1.82MPa, 6.4mm, unannealed (ASTM D648)
Flame Characteristics
- Flame Retardancy: 2.5mm V-0, classified with high thermal resistance and stability.
Processing Guide
- Drying Temperature: 80~90℃
- Drying Time: 3~4 hours
- Injection Temperature: 200~230℃
- Mold Temperature: 40~60℃
- Screw Speed: 30~60 rpm
Use & Applications
- Blood Pressure Monitors
- Oxygen Concentrators
- Power Supply Housings / Development
- Sockets and Electrical Connectors
Features & Benefits
Superior Flame Retardant Safety
This material achieves a UL94 V-0 rating at 2.5mm, significantly enhancing end-product safety and helping you meet strict international safety standards for electronics and medical devices.
Excellent Thermal Resistance
With a Heat Deflection Temperature of 85°C, AF367H maintains structural integrity under thermal stress, ensuring reliable performance in devices that generate heat during operation.
Easy and Stable Processing
Its high melt flow rate (30 g/10min) ensures excellent fill characteristics and short cycle times during injection molding, boosting your production efficiency and reducing manufacturing costs.