LG Chem ABS HI140
LG ABS HI140 General Grade
LG ABS HI140 is a super high-impact ABS resin designed for injection molding. It delivers exceptional durability and a bright white color, making it ideal for demanding safety and automotive components.
Typical property data
Physical Properties
- Melt Flow Index: 13 g/10min (220℃, 10kg, ASTM D1238)
Mechanical Properties
- Tensile Strength at Yield: 41 MPa (23℃, 50mm/min, 3.2mm, ASTM D638)
- Flexural Strength: 62 MPa (23℃, 10mm/min, 6.4mm, ASTM D790)
- Flexural Modulus: 1800 MPa (23℃, 10mm/min, 6.4mm, ASTM D790)
- Izod Impact Strength (Notched): 40 J/m (6.4mm, 23℃, ASTM D256)
- Rockwell Hardness (R-Scale): 102 (ASTM D785)
Thermal Properties
- Heat Deflection Temperature: 85℃ (Edgewise, 1.82MPa, 6.4mm, Annealed, ASTM D648)
Impact Properties
- High Impact Strength: Specifically designed for improved resilience.
Injection Molding Guidelines
- Drying Temperature: 75~85℃
- Drying Time: 2~4 hours
- Injection Temperature: 180~240℃
- Mold Temperature: 40~80℃
- Screw Speed: 30~60 rpm
Features & Benefits
Exceptional Impact Resistance
With an outstanding notched Izod impact strength, LG ABS HI140 absorbs high-energy impacts, enhancing product safety and longevity in rugged use cases.
Easy, Consistent Processing
Its balanced melt flow ensures easy injection molding with excellent fill characteristics, leading to high production efficiency and superior surface finish.
Reliable Bright White Color
The material is engineered for a bright, consistent white appearance, reducing the need for additional pigments and ensuring aesthetic quality part after part.
Use & Applications
- Safety Helmets (Industrial, Motorcycle)
- High-Durability Motorcycle Parts