LG Chem ABS HP100H
Plastic Granules
LG ABS HP100H General Grade
LG ABS HP100H is a high-impact, injection molding grade resin from LG Chem. It delivers exceptional low-temperature toughness, high stiffness, and an excellent surface finish ideal for painting, making it perfect for demanding consumer and industrial applications.
Typical property data
Physical Properties
- Melt Flow Index: 6 g/10min (220°C, 10kg; ASTM D1238)
Mechanical Properties
- Tensile Strength at Yield: 42 MPa (23°C, 50mm/min, 3.2mm specimen; ASTM D638)
- Flexural Strength: 63 MPa (23°C, 10mm/min, 6.4mm specimen; ASTM D790)
- Flexural Modulus: 2100 MPa (23°C, 10mm/min, 6.4mm specimen; ASTM D790)
- Izod Impact Strength (Notched): 45 J/m (23°C, 6.4mm specimen; ASTM D256)
- Rockwell Hardness: 102, R-Scale (ASTM D785)
Thermal Properties
- Heat Deflection Temperature (HDT): 84°C (Edgewise, 1.82 MPa load, 6.4mm specimen, Unannealed; ASTM D648)
Impact Properties
- Multi-axial impact strength
Injection Molding Parameters
- Drying Temperature: 70–80°C
- Drying Time: 2–4 hours
- Injection Temperature: 200–250°C
- Mold Temperature: 40–80°C
- Screw Speed: 30–60 rpm
Features & Benefits
Exceptional Low-Temperature Toughness
This resin maintains high impact strength in cold environments, preventing cracks and ensuring product durability and reliability for outdoor or refrigerated use.
Superior Surface for Painting
HP100H provides a consistently smooth surface, ensuring flawless paint adhesion and a high-quality, glossy finish that enhances the final product’s aesthetic appeal.
High Strength and Stiffness
The material offers outstanding structural integrity and rigidity, allowing for the design of durable parts that resist deformation under load during everyday use.
Use & Applications
- Helmets
- Watches
- Refrigerators