LG Chem ABS HT700
LG ABS HT700 General Grade
LG ABS HT700 is a high-stiffness ABS resin engineered for injection molding. It delivers exceptional structural integrity and reliability for demanding technical applications.
Associated Documents
ISO TDS
ASTM TDS
MSDS
ROHS
UL Yellow Card
Typical property data
Physical Properties
- Specific Gravity: 1.05 (ISO 1183)
- Mold Shrinkage: 0.4−0.7%, 3.2mm at 23°C (ISO 294-4)
- Melt Flow Rate (MFR): 18 g/10min, 220°C, 10 kg (ISO 1133)
Mechanical Properties
- Tensile Strength at Yield: 45 MP, 23°C, 50 mm/min, 4mm (ISO 527)
- Tensile Elongation at Break: ≥10%, 23°C, 50 mm/min, 4mm (ISO 527)
- Flexural Strength: 73 MPa, 23∘C, 2 mm/min, 4mm (ISO 178)
- Flexural Modulus: 2500 MPa, 23°C, 2 mm/min, 4mm (ISO 178)
- Rockwell Hardness (R-Scale): 113 (ISO 2039)
Impact Properties
- Izod Impact Strength (Notched, 4mm):
- 19 kJ/m², 23℃ (ISO 180/1A)
- 8 kJ/m², −30℃ (ISO 180/1A)
- Charpy Impact Strength (Notched, 4mm):
- 18 kJ/m², 23℃ (ISO 179/1eA)
- 8 kJ/m², −30℃ (ISO 179/1eA)
Thermal Properties
- Heat Deflection Temperature (HDT): 83℃ , 1.8 MPa, 4mm, Unannealed (ISO 75)
- Vicat Softening Temperature: 95℃ , 50 N,50℃ /h (ISO 306)
Injection Molding Parameters
- Drying Temperature: 70−80℃
- Drying Time: 3−4 hrs
- Injection Temperature: 200−250℃
- Mold Temperature: 40−80℃
- Screw Speed: 30−60 rpm
Features & Benefits
Superior Structural Rigidity
HT700 provides outstanding stiffness and strength, ensuring dimensional stability and preventing deformation in precision parts under load.
Excellent Processability
With a balanced melt flow, it offers easy injection molding, fast cycle times, and high-quality surface finishes, boosting your production efficiency.
Certified Safety & Compliance
This material is RoHS, REACH, and UL 94 HB compliant, guaranteeing it meets stringent international safety and environmental regulations for global markets.
Use & Applications
- Piano Keys
- Bobbins
- Electrical/Electronic Products
- Miscellaneous Goods