LG Chem ABS RS650
Plastic Granules
LG ABS RS650 Extrusion Grade
LG ABS RS650 is a high-performance extrusion-grade ABS resin engineered to deliver exceptional impact resistance and structural rigidity, making it ideal for demanding sheet and profile applications.
Typical property data
Physical Properties
- Specific Gravity: 1.04 (ASTM D792)
- Mold Shrinkage: 0.4 ~ 0.7% (ASTM D955)
- Melt Flow Index: 6 g/10min (220°C, 10kg, ASTM D1238)
Mechanical Properties
- Tensile Strength at Yield: 48 MPa (23°C, 50mm/min, 3.2mm, ASTM D638)
- Tensile Elongation at Break: ≥10% (23°C, 50mm/min, 3.2mm, ASTM D638)
- Flexural Strength: 79 MPa (23°C, 10mm/min, 6.4mm, ASTM D790)
- Flexural Modulus: 2500 MPa (23°C, 10mm/min, 6.4mm, ASTM D790)
- Rockwell Hardness: 108 (R-Scale, ASTM D785)
Impact Properties
- Izod Impact Strength, Notched:
- 3.2mm at 23°C: 340 J/m (ASTM D256)
- 3.2mm at -30°C: 150 J/m (ASTM D256)
- 6.4mm at 23°C: 320 J/m (ASTM D256)
- 6.4mm at -30°C: 140 J/m (ASTM D256)
Thermal Properties
- Heat Deflection Temperature: 90°C (Edgewise, 1.82MPa, 6.4mm, Unannealed, ASTM D648)
- Vicat Softening Temperature: 98°C (50N, 50°C/h, ASTM D1525)
Injection Molding/Processing
- Drying Temperature: 80 ~ 90°C
- Drying Time: 3 ~ 4 hours
- Moisture Content: ~0.01%
- Extrusion Temperature: 180 ~ 250°C
Features & Benefits
Superior Impact Resistance
With outstanding Izod impact strength, ABS RS650 LG Chem ensures your extruded profiles and sheets can withstand physical shocks and harsh handling without cracking or breaking.
Excellent Stiffness & Strength
This material provides high flexural modulus and tensile strength, guaranteeing dimensional stability and structural integrity for load-bearing components like pipes and architectural panels.
Good Thermal Stability
Featuring a heat deflection temperature of 90°C, components made from LG ABS RS650 maintain their shape and performance in elevated temperature environments.
Use & Applications
- General Extruded Sheet
- Pipe
- Bathroom Ceiling