LG Chem ABS SH610A
Plastic Granules
LG ABS SH610A Extrusion Grade
LG ABS SH610A is an extrusion-grade ABS resin engineered for exceptional impact strength and reliable processability. Ideal for demanding sheet extrusion applications where durability and consistency are critical.
Typical property data
Physical Properties
- Specific Gravity: 1.04 (ASTM D792)
- Mold Shrinkage: 0.4–0.7% (ASTM D955)
- Melt Flow Index: 5 g/10 min (220℃, 10kg, ASTM D1238)
Mechanical Properties
- Tensile Strength at Yield: 41 MPa (23℃, ASTM D638)
- Tensile Elongation at Break: Minimum 10% (23℃, ASTM D638)
- Flexural Strength: 63 MPa (23℃, ASTM D790)
- Flexural Modulus: 2050 MPa (23℃, ASTM D790)
- Rockwell Hardness (R-Scale): 97 (ASTM D785)
Impact Properties
- Izod Impact Strength (Notched, 3.2 mm, ASTM D256):
- 23℃: 490 J/m
- -30℃: 210 J/m
- Izod Impact Strength (Notched, 6.4 mm, ASTM D256):
- 23℃: 420 J/m
- -30℃: 190 J/m
Thermal Properties
- Heat Deflection Temperature: 87℃ (1.82 MPa, ASTM D648)
- Vicat Softening Temperature: 94℃ (50N, ASTM D1525)
Processing Guide
- Drying Temperature: 80–90℃
- Drying Time: 3–4 hours
- Moisture Content: ~0.01%
- Extrusion Temperature: 180–250℃
Features & Benefits
Exceptional Impact Resistance
With high Izod impact strength (up to 490 J/m), SH610A ensures durability in tough environments, reducing part failure and extending product life.
Easy Extrusion Processing
Designed for smooth extrusion between 180–250°C, this resin offers excellent melt stability and low moisture uptake, minimizing production downtime.
RoHS & UL Certified
Compliant with EU RoHS Directive and rated UL 94 HB, SH610A meets global safety and environmental standards, simplifying compliance for international buyers.
Use & Applications
- General extruded sheets
- Protective covers and enclosures
- Automotive interior trim components
- Point-of-sale displays and signage
- Furniture and sanitary profiles