LG Chem MABS TR530F
Plastic Granules
LG ABS TR530F Transparent Grade
LG Chem ABS TR530F is a premium transparent ABS resin engineered for injection molding. It delivers an exceptional balance of high optical clarity, superior impact strength, and a soft-touch finish, making it ideal for demanding and aesthetically sensitive applications.
Typical property data
Physical Properties
- Specific Gravity: 1.06 (ASTM D792)
- Mold Shrinkage: 0.4 – 0.7% (ASTM D955)
- Melt Flow Index (MFI): 10 g/10min @ 220℃, 10kg (ASTM D1238)
Mechanical Properties
- Tensile Strength at Yield: 33 MPa (ASTM D638, 23℃, 50mm/min, 3.2mm)
- Tensile Elongation at Yield: ≥5% (ASTM D638, 23℃, 50mm/min, 3.2mm)
- Tensile Elongation at Break: ≥25% (ASTM D638, 23℃, 50mm/min, 3.2mm)
- Flexural Strength: 49 MPa (ASTM D790, 23℃, 10mm/min, 6.4mm)
- Flexural Modulus: 1500 MPa (ASTM D790, 23℃, 10mm/min, 6.4mm)
- Rockwell Hardness: 88, R-Scale (ASTM D785)
Impact Properties
- Notched Izod Impact Strength (3.2mm, 23℃): 235 J/m (ASTM D256)
- Notched Izod Impact Strength (3.2mm, -30℃): 90 J/m (ASTM D256)
- Notched Izod Impact Strength (6.4mm, 23℃): 235 J/m (ASTM D256)
- Notched Izod Impact Strength (6.4mm, -30℃): 90 J/m (ASTM D256)
Thermal Properties
- Heat Deflection Temperature (Unannealed):
- 74℃ @ 1.82 MPa (ASTM D648)
- 82℃ @ 0.46 MPa (ASTM D648)
- Heat Deflection Temperature (Annealed):
- 80℃ @ 1.82 MPa (ASTM D648)
- 85℃ @ 0.46 MPa (ASTM D648)
- Vicat Softening Temperature: 81℃ @ 50N, 50℃/h (ASTM D1525)
Optical Properties
- Haze: 3% (ASTM D1003)
- Luminous Transmittance: 89% (ASTM D1003, 3.2mm)
Processing Guide
- Drying Temperature: 70 – 80℃
- Drying Time: 3 – 4 hours
- Injection Temperature: 200 – 250℃
- Mold Temperature: 40 – 80℃
- Screw Speed: 30 – 60 rpm
Features & Benefits
Superior Optical Clarity
Experience crystal-clear transparency with a luminous transmittance of 89% and low haze (3%), ensuring your products look pristine and professional right out of the mold.
Exceptional Impact Resistance
Withstand everyday drops and impacts thanks to its high notched Izod strength (235 J/m), enhancing product durability and reducing failure rates for end-users.
Excellent Processing Versatility
Enjoy easy molding with a wide processing window (200-250°C) and good melt flow (10 g/10min), leading to faster cycle times and high-quality, consistent parts.
Use & Applications
Artificial Nail