LG Chem ABS XR410
Plastic Granules
LG ABS XR410 Heat Resistant Grade
LG ABS XR410 from LG Chem is a high-heat ABS resin engineered for interior parts. It features low gloss, very low VOC emissions, and does not require painting, simplifying your manufacturing process.
Typical property data
Physical Properties
- Specific Gravity: 1.05 (ISO 1183)
- Mold Shrinkage: 0.4% – 0.8% (ISO 294-4)
- Melt Flow Rate (MFR): 7 g/10 min, tested at 220℃, 10 kg load (ISO 1133)
Mechanical Properties
- Tensile Strength at Yield: 50 MPa (23℃, 50 mm/min, 4 mm, ISO 527)
- Tensile Elongation at Yield: ≥ 5% (ISO 527)
- Tensile Elongation at Break: ≥ 10% (ISO 527)
- Tensile Modulus: 2300 MPa (ISO 527)
- Flexural Strength: 70 MPa (ISO 178)
- Flexural Modulus: 2350 MPa (ISO 178)
- Rockwell Hardness: R-Scale, 110 (ISO 2039)
Impact Properties
- Izod Impact Strength (Notched):
- 15 kJ/m² at 23℃ (ISO 180/1A)
- 8 kJ/m² at -30℃ (ISO 180/1A)
- Charpy Impact Strength (Notched):
- 13 kJ/m² at 23℃ (ISO 179/1eA)
- 8 kJ/m² at -30℃ (ISO 179/1eA)
Thermal Properties
- Heat Deflection Temperature (HDT):
- 86℃ (1.8 MPa, 4 mm, unannealed, ISO 75)
- 94℃ (0.45 MPa, 4 mm, unannealed, ISO 75)
- 94℃ (1.8 MPa, 4 mm, annealed, ISO 75)
- 99℃ (0.45 MPa, 4 mm, annealed, ISO 75)
- Vicat Softening Point: 107℃ (50 N, 50℃/h, ISO 306)
Flame Characteristics
- Flammability: HB for thicknesses 1.5 mm and 3.0 mm (UL 94)
Processing Data
- Drying Temperature: 80 – 90℃
- Drying Time: 3 – 4 hours
- Injection Temperature: 220 – 290℃
- Mold Temperature: 40 – 80℃
- Screw Speed: 30 – 60 rpm
Features & Benefits
Exceptional Heat Resistance
With a Heat Deflection Temperature up to 108°C, XR410 maintains its shape and strength in high-temperature environments, such as car interiors under direct sunlight, ensuring long-term part reliability.
Low VOC for Healthier Interiors
This material is formulated for minimal Total Volatile Organic Compound (TVOC) emission. It helps you meet stringent indoor air quality standards for automotive cabins, creating a safer and more comfortable environment.
Ready-to-Use Low Gloss Finish
XR410 provides a consistent, non-reflective low-gloss surface directly out of the mold. This eliminates the need for secondary painting, reducing production costs and time for parts like dashboards and trim.
Use & Applications
- Cockpit Modules & Instrument Panels
- Door Trims and Interior Handles
- Various Interior Trim Components