SABIC® PC Resin PC2200R
Plastic Granules
Sabic PC2200R Injection Molding Grade High-flow Heat-stabilized
Sabic PC2200R is a high-flow, heat-stabilized polycarbonate with built-in mold release. It simplifies production for high-volume, general-purpose molding, delivering excellent performance and faster cycle times.
Typical property data
Physical Properties
- Specific Gravity: 1.2 (ASTM D792, ISO 1183)
- Water Absorption (23°C/Saturated): 0.35% (ASTM D570, ISO 62-1)
- Melt Flow Rate (300°C/1.2 kg): 22 g/10 min (ASTM D1238)
- Mold Shrinkage (Flow, 3.2 mm): 0.5–0.7% (SABIC Method)
Mechanical Properties
- Tensile Stress (Yield, 50 mm/min): 63 MPa (ASTM D638, ISO 527)
- Tensile Modulus (1 mm/min): 2350 MPa (ASTM D638, ISO 527)
- Flexural Stress (Yield, 2 mm/min): 90 MPa (ASTM D790, ISO 178)
- Flexural Modulus (2 mm/min): 2300 MPa (ASTM D790, ISO 178)
- Rockwell Hardness (Scale R): 120 (ASTM D785, ISO 2039-2)
Impact Properties
- Izod Impact Strength (Notched, 23°C): 640 J/m (ASTM D256)
- Izod Impact Strength (Notched, 23°C): 65 kJ/m² (ISO 180/1A)
- Izod Impact Strength (Notched, -30°C): 12 kJ/m² (ISO 180/1A)
Thermal Properties
- Vicat Softening Temperature (Rate B/50): 140°C (ASTM D1525, ISO 306)
- Heat Deflection Temperature (0.45 MPa): 133°C (ASTM D648, ISO 75/Bf)
- Heat Deflection Temperature (1.8 MPa): 122°C (ASTM D648, ISO 75/Af)
- Thermal Conductivity: 0.2 W/m-°C (ASTM C177, ISO 8302)
Optical Properties
- Light Transmission (2.54 mm): 88–90% (ASTM D1003)
- Haze (2.54 mm): <0.8% (ASTM D1003)
- Refractive Index: 1.586 (ASTM D542, ISO 489)
Electrical Properties
- Volume Resistivity: >1.E+15 Ω·cm (ASTM D257, IEC 60093)
- Dielectric Strength (1.6 mm): 27 kV/mm (ASTM D149, IEC 60243-1)
- Relative Permittivity (60 Hz): 3 (ASTM D150, IEC 60250)
- Dissipation Factor (60 Hz): 0.001 (ASTM D150, IEC 60250)
Flame Characteristics
- UL 94 Flame Class Rating: 94V-2 (1.5 mm thickness)
Injection Molding Guidelines
- Drying Temperature: 120°C
- Drying Time: 2–4 hours
- Maximum Moisture Content: 0.02%
- Melt Temperature: 280–300°C
- Mold Temperature: 80–100°C
- Nozzle Temperature: 270–290°C
Features & Benefits
Superior High-Flow Molding
The high melt flow rate (MFR=22) of Sabic PC2200R ensures easy filling of complex and thin-walled molds. This results in fewer short shots and higher productivity for intricate parts.
Exceptional Impact Resistance
This material offers outstanding toughness, with a Notched Izod Impact of 640 J/m. Your components will be durable and resistant to cracking or breaking from sudden impacts during use.
Built-In Mold Release Agent
The internal mold release in SABIC PC Resin PC2200R facilitates easier part ejection. This significantly reduces cycle times and minimizes mold fouling, leading to lower operational costs.
Use & Applications
- Consumer Electronics Housings
- Automotive Interior Components
- Electrical Enclosures and Connectors
- Industrial Parts and Housings
- Various Durable Consumer Goods