XENOY™ Resin PC PBT 1760T
Plastic Granules
Associated Documents
TDS - Europe
Typical property data
Physical Properties
- Density: 1.3 g/cm³ (ISO 1183)
- Mold Shrinkage on Tensile Bar, Flow: 0.5–0.9% (SABIC Method)
- Water Absorption, 23°C Saturated: 0.5% (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.15% (ISO 62)
- Melt Volume Rate, MVR at 250°C / 5.0 kg: 14 cm³/10 min (ISO 1133)
- Glass Reinforcement Content: 11% glass reinforced (Datasheet Description)
Mechanical Properties
- Tensile Stress at Break, 5 mm/min: 90 MPa (ISO 527)
- Tensile Strain at Break, 5 mm/min: 3% (ISO 527)
- Tensile Modulus, 1 mm/min: 4500 MPa (ISO 527)
- Flexural Stress at Break, 2 mm/min: 140 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 4000 MPa (ISO 178)
- Ball Indentation Hardness, H358/30: 105 MPa (ISO 2039-1)
- Hardness, Rockwell R: 113 (ISO 2039-2)
Impact Properties
- Izod Impact, Unnotched, 80 × 10 × 4 mm, +23°C: 30 kJ/m² (ISO 180/1U)
- Izod Impact, Unnotched, 80 × 10 × 4 mm, -30°C: 30 kJ/m² (ISO 180/1U)
- Izod Impact, Notched, 80 × 10 × 4 mm, +23°C: 3 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, 0°C: 3 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -30°C: 3 kJ/m² (ISO 180/1A)
- Charpy V-Notch Edgewise, 80 × 10 × 4 mm, Span 62 mm, +23°C: 4 kJ/m² (ISO 179/1eA)
- Charpy V-Notch Edgewise, 80 × 10 × 4 mm, Span 62 mm, -30°C: 3 kJ/m² (ISO 179/1eA)
- Charpy Unnotched Edgewise, 80 × 10 × 4 mm, Span 62 mm, +23°C: 35 kJ/m² (ISO 179/1eU)
- Charpy Unnotched Edgewise, 80 × 10 × 4 mm, Span 62 mm, -30°C: 35 kJ/m² (ISO 179/1eU)
Thermal Properties
- Thermal Conductivity: 0.19 W/m·°C (ISO 8302)
- Coefficient of Thermal Expansion, Flow, 23°C to 80°C: 4.0E-05 1/°C (ISO 11359-2)
- Coefficient of Thermal Expansion, Cross-Flow, 23°C to 80°C: 1.1E-04 1/°C (ISO 11359-2)
- Ball Pressure Test, 75°C ± 2°C: Passes (IEC 60695-10-2)
- Vicat Softening Temperature, Rate B/50: 135°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 130°C (ISO 306)
- HDT/Be, 0.45 MPa, Edgewise, 120 × 10 × 4 mm, Span 100 mm: 115°C (ISO 75/Be)
- HDT/Ae, 1.8 MPa, Edgewise, 120 × 10 × 4 mm, Span 100 mm: 105°C (ISO 75/Ae)
Electrical Properties
- Volume Resistivity: >1.0E+14 Ω·cm (IEC 60093)
- Surface Resistivity, ROA: >1.0E+15 Ω (IEC 60093)
- Dielectric Strength, In Oil, 3.2 mm: 17 kV/mm (IEC 60243-1)
- Relative Permittivity, 1 MHz: 3.1 (IEC 60250)
- Relative Permittivity, 50/60 Hz: 3.3 (IEC 60250)
- Dissipation Factor, 50/60 Hz: 0.002 (IEC 60250)
- Dissipation Factor, 1 MHz: 0.02 (IEC 60250)
Flame Characteristics
- UL Compliant Flame Class Rating, 94HB, 1.5 mm
Injection Molding Parameters
- Drying Temperature: 100–110°C
- Drying Time: 2–4 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 255–270°C
- Nozzle Temperature: 250–265°C
- Front Zone 3 Temperature: 250–270°C
- Middle Zone 2 Temperature: 240–265°C
- Rear Zone 1 Temperature: 230–250°C
- Hopper Temperature: 40–60°C
- Mold Temperature: 60–100°C
Use & Applications
- Door handles
- Mirror housings
- Automotive exterior parts
- Complex molded components requiring easy flow and stable dimensions