XENOY™ Resin PC PBT 5220U
Plastic Granules
XENOY™ Resin 5220U Impact modified PBT+PC Alloy
XENOY™ Resin 5220U is an unreinforced PBT+PC alloy with impact modification. It offers 710 J/m notched Izod impact at 23°C and 530 J/m at -30°C. It supports UV property retention, chemical resistance, and stable molding with 16 g/10 min MFR.
Typical property data
Physical Properties
- Specific Gravity: 1.21 (ASTM D792)
- Specific Volume: 0.83 cm³/g (ASTM D792)
- Density: 1.22 g/cm³ (ISO 1183)
- Mold Shrinkage, Flow, 3.2 mm: 0.8–1.0% (SABIC Method)
- Mold Shrinkage on Tensile Bar, X-Flow: 0.8–1.1% (SABIC Method)
- Water Absorption, 23°C Saturated: 0.5% (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.15% (ISO 62)
- Melt Flow Rate, 250°C / 5.0 kg: 16 g/10 min (ISO 1133)
- Melt Volume Rate, 250°C / 5.0 kg: 15 cm³/10 min (ISO 1133)
- Melt Volume Rate, 250°C / 5 kg: 15 cm³/10 min (ASTM D1238)
Mechanical Properties
- Tensile Stress at Yield, Type I, 50 mm/min: 53 MPa (ASTM D638)
- Tensile Stress at Break, Type I, 50 mm/min: 51 MPa (ASTM D638)
- Tensile Strain at Yield, Type I, 50 mm/min: 4% (ASTM D638)
- Tensile Strain at Break, Type I, 50 mm/min: 120% (ASTM D638)
- Tensile Modulus, 50 mm/min: 2250 MPa (ASTM D638)
- Tensile Modulus, 5 mm/min: 2250 MPa (ASTM D638)
- Flexural Stress at Yield, 1.3 mm/min, 50 mm Span: 84 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm Span: 2030 MPa (ASTM D790)
- Tensile Stress at Yield, 50 mm/min: 50 MPa (ISO 527)
- Tensile Stress at Break, 50 mm/min: 50 MPa (ISO 527)
- Tensile Strain at Yield, 50 mm/min: 4% (ISO 527)
- Tensile Strain at Break, 50 mm/min: 120% (ISO 527)
- Tensile Modulus, 1 mm/min: 2050 MPa (ISO 527)
- Flexural Stress at Yield, 2 mm/min: 80 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 2000 MPa (ISO 178)
Impact Properties
- Notched Izod Impact, 23°C: 710 J/m (ASTM D256)
- Notched Izod Impact, -30°C: 530 J/m (ASTM D256)
- Notched Izod Impact, -40°C: 299 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 60 J (ASTM D3763)
- Notched Izod Impact, 80 × 10 × 4 mm, +23°C: 50 kJ/m² (ISO 180/1A)
- Notched Izod Impact, 80 × 10 × 4 mm, -30°C: 30 kJ/m² (ISO 180/1A)
- Charpy Impact, 23°C, V-Notch Edgewise, 80 × 10 × 4 mm, Span 62 mm: 55 kJ/m² (ISO 179/1eA)
Thermal Properties
- Vicat Softening Temperature, Rate B/50: 122°C (ASTM D1525)
- Vicat Softening Temperature, Rate B/50: 120°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 125°C (ISO 306)
- HDT, 1.82 MPa, 3.2 mm, Unannealed: 84°C (ASTM D648)
- HDT, 0.45 MPa, 6.4 mm, Unannealed: 107°C (ASTM D648)
- HDT, 1.82 MPa, 6.4 mm, Unannealed: 99°C (ASTM D648)
- HDT/Af, 1.8 MPa Flatwise, 80 × 10 × 4 mm, Span 64 mm: 75°C (ISO 75/Af)
- CTE, -40°C to 40°C, Flow: 9.5E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, X-Flow: 9.0E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, Flow: 9.5E-05 1/°C (ISO 11359-2)
- CTE, -40°C to 40°C, X-Flow: 9.0E-05 1/°C (ISO 11359-2)
- Relative Temperature Index, Electrical: 75°C (UL 746B)
- Relative Temperature Index, Mechanical with Impact: 75°C (UL 746B)
- Relative Temperature Index, Mechanical without Impact: 75°C (UL 746B)
Electrical Properties
- Arc Resistance, Tungsten PLC: 5 PLC Code (ASTM D495)
- Hot Wire Ignition PLC: 3 PLC Code (UL 746A)
- High Voltage Arc Tracking Rate PLC: 0 PLC Code (UL 746A)
- High Ampere Arc Ignition, Surface PLC: 0 PLC Code (UL 746A)
- Comparative Tracking Index, UL PLC: 1 PLC Code (UL 746A)
Flame Characteristics
- UL Yellow Card Link: E207780-103219926
- UL Recognized 94HB Flame Class Rating: 1.5 mm (UL 94)
- UV-Light, Water Exposure / Immersion: F2 (UL 746C)
Injection Molding Processing
- Drying Temperature: 110°C
- Drying Time: 4–6 hrs
- Drying Time, Cumulative: 8 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 260–275°C
- Nozzle Temperature: 255–270°C
- Front Zone 3 Temperature: 255–275°C
- Middle Zone 2 Temperature: 250–270°C
- Rear Zone 1 Temperature: 245–265°C
- Mold Temperature: 65–90°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 50–80 rpm
- Shot to Cylinder Size: 50–80%
- Vent Depth: 0.013–0.02 mm
Sheet Extrusion Processing
- Drying Temperature: 110–115°C
- Drying Time: 4–6 hrs
- Drying Time, Cumulative: 8 hrs
- Maximum Moisture Content: 0–0.02%
- Melt Temperature: 245–275°C
- Barrel Zone 1 Temperature: 170–205°C
- Barrel Zone 2 Temperature: 195–255°C
- Barrel Zone 3 Temperature: 205–280°C
- Barrel Zone 4 Temperature: 205–280°C
- Adapter Temperature: 225–280°C
- Die Temperature: 230–280°C
- Roll Stack Temperature, Top: 70–80°C
- Roll Stack Temperature, Middle: 75–80°C
- Roll Stack Temperature, Bottom: 80–95°C
Use & Applications
- Automotive exterior components
- unpainted exterior parts
- outdoor molded applications requiring UV stability