XENOY™ Resin PC PBT 6620
Plastic Granules
XENOY™ Resin 6620 Impact-modified Thermoplastic PC PBT Alloy
XENOY™ Resin 6620 is an unreinforced PC+PBT alloy with impact modification. It delivers 850 J/m notched Izod impact at 23°C and 175% tensile strain at break. Suitable for injection molding with 250–290°C melt temperature.
Typical property data
Physical Properties
- Specific Gravity: 1.20 (ASTM D792)
- Mold Shrinkage, Flow, 3.2 mm: 1.5–2.0% (SABIC Method)
Mechanical Properties
- Tensile Stress at Yield, Type I, 50 mm/min: 43 MPa (ASTM D638)
- Tensile Strain at Break, Type I, 50 mm/min: 175% (ASTM D638)
- Flexural Stress at Yield, 1.3 mm/min, 50 mm span: 64 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm span: 1720 MPa (ASTM D790)
Impact Properties
- Notched Izod Impact Strength, 23°C: 850 J/m (ASTM D256)
Thermal Properties
- Heat Deflection Temperature, 1.82 MPa, 6.4 mm, Unannealed: 60°C (ASTM D648)
Processing Parameters
- Recommended Drying Temperature: 120°C
- Recommended Drying Time: 3–4 hours
- Maximum Cumulative Drying Time: 12 hours
- Recommended Melt Temperature: 250–290°C
- Recommended Mold Temperature: 55–80°C
Use & Applications
- Automotive exterior and interior parts
- Housings, trims, and parts used in cold environments