XENOY™ Resin PC PBT CL100
Plastic Granules
XENOY™ Resin PC PBT CL100
XENOY™ Resin CL100 is an unfilled, impact-modified, UV-stabilized PC/PBT blend. It offers strong solvent resistance, low-temperature ductility, and high impact strength. It is designed for unpainted exterior automotive parts and supports stable injection molding.
Typical property data
Physical Properties
- Specific Gravity: 1.22 (ASTM D792)
- Density: 1.22 g/cm³ (ISO 1183)
- Mold Shrinkage, flow, 3.2 mm: 0.7–1% (SABIC method)
- Melt Flow Rate, 250°C/5.0 kgf: 14 g/10 min (ASTM D1238)
- Melt Volume Rate, MVR at 250°C/5.0 kg: 13 cm³/10 min (ISO 1133)
- Water Absorption, 23°C/saturated: 0.5% (ISO 62-1)
- Moisture Absorption, 23°C/50% RH: 0.15% (ISO 62)
Mechanical Properties
- Tensile Stress, yield, Type I, 50 mm/min: 56 MPa (ASTM D638)
- Tensile Stress, break, Type I, 50 mm/min: 55 MPa (ASTM D638)
- Tensile Strain, yield, Type I, 50 mm/min: 5% (ASTM D638)
- Tensile Strain, break, Type I, 50 mm/min: 100% (ASTM D638)
- Tensile Modulus, 5 mm/min: 2200 MPa (ASTM D638)
- Flexural Stress, yield, 1.3 mm/min, 50 mm span: 85 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm span: 2050 MPa (ASTM D790)
- Taber Abrasion, CS-17, 1 kg: 30 mg/1000 cycles (SABIC method)
- Tensile Stress, yield, 50 mm/min: 55 MPa (ISO 527)
- Tensile Stress, break, 50 mm/min: 56 MPa (ISO 527)
- Tensile Strain, yield, 50 mm/min: 5% (ISO 527)
- Tensile Strain, break, 50 mm/min: 100% (ISO 527)
- Tensile Modulus, 1 mm/min: 2150 MPa (ISO 527)
- Flexural Stress, yield, 2 mm/min: 80 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 2050 MPa (ISO 178)
- Ball Indentation Hardness, H358/30: 96 MPa (ISO 2039-1)
Impact Properties
- Izod Impact, notched, 23°C: 700 J/m (ASTM D256)
- Izod Impact, notched, 0°C: 600 J/m (ASTM D256)
- Izod Impact, notched, -30°C: 170 J/m (ASTM D256)
- Izod Impact, notched, -40°C: 160 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 50 J (ASTM D3763)
- Izod Impact, unnotched, 80 × 10 × 4 mm, +23°C: NB (ISO 180/1U)
- Izod Impact, unnotched, 80 × 10 × 4 mm, -30°C: NB (ISO 180/1U)
- Izod Impact, notched, 80 × 10 × 4 mm, +23°C: 50 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, 0°C: 45 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, -30°C: 20 kJ/m² (ISO 180/1A)
- Charpy Impact, V-notch edgewise, 23°C, 80 × 10 × 4 mm, span 62 mm: 55 kJ/m² (ISO 179/1eA)
- Charpy Impact, V-notch edgewise, -30°C, 80 × 10 × 4 mm, span 62 mm: 20 kJ/m² (ISO 179/1eA)
- Charpy Impact, unnotched edgewise, 23°C, 80 × 10 × 4 mm, span 62 mm: NB (ISO 179/1eU)
- Charpy Impact, unnotched edgewise, -30°C, 80 × 10 × 4 mm, span 62 mm: NB (ISO 179/1eU)
Thermal Properties
- Vicat Softening Temperature, Rate B/50: 125°C (ASTM D1525)
- Heat Deflection Temperature, 1.82 MPa, 3.2 mm, unannealed: 90°C (ASTM D648)
- Coefficient of Thermal Expansion, -40°C to 40°C, flow: 9.0E-05 1/°C (ASTM E831)
- Coefficient of Thermal Expansion, -40°C to 40°C, cross-flow: 9.0E-05 1/°C (ASTM E831)
- Thermal Conductivity: 0.18 W/m·°C (ISO 8302)
- Coefficient of Thermal Expansion, 23°C to 80°C, flow: 9.0E-05 1/°C (ISO 11359-2)
- Coefficient of Thermal Expansion, 23°C to 80°C, cross-flow: 9.0E-05 1/°C (ISO 11359-2)
- Vicat Softening Temperature, Rate A/50: 160°C (ISO 306)
- Vicat Softening Temperature, Rate B/50: 125°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 127°C (ISO 306)
- Heat Deflection Temperature, HDT/Ae, 1.8 MPa, edgewise, 120 × 10 × 4 mm, span 100 mm: 90°C (ISO 75/Ae)
- Heat Deflection Temperature, HDT/Bf, 0.45 MPa, flatwise, 80 × 10 × 4 mm, span 64 mm: 110°C (ISO 75/Bf)
- Heat Deflection Temperature, HDT/Af, 1.8 MPa, flatwise, 80 × 10 × 4 mm, span 64 mm: 90°C (ISO 75/Af)
Electrical Properties
- Volume Resistivity: >1.0E+14 Ω·cm (IEC 60093)
- Surface Resistivity, ROA: >1.0E+15 Ω (IEC 60093)
- Dielectric Strength, short-time, 1.0 mm: 18 kV/mm (IEC 60243-1)
- Dielectric Strength, in oil, 3.2 mm: 17 kV/mm (IEC 60243-1)
- Relative Permittivity, 1 MHz: 3.3 (IEC 60250)
- Relative Permittivity, 50/60 Hz: 3.3 (IEC 60250)
- Dissipation Factor, 50/60 Hz: 0.002 (IEC 60250)
- Dissipation Factor, 1 MHz: 0.02 (IEC 60250)
Flame Characteristics
- UL Recognized, 94HB Flame Class Rating: 1.5 mm (UL 94)
Processing Parameters
- Drying Temperature: 90–100°C
- Drying Time: 2–4 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 255–270°C
- Nozzle Temperature: 250–265°C
- Front Zone 3 Temperature: 250–270°C
- Middle Zone 2 Temperature: 240–265°C
- Rear Zone 1 Temperature: 230–250°C
- Hopper Temperature: 40–60°C
- Mold Temperature: 60–80°C
Use & Applications
- Unpainted exterior automotive applications
- Body components
- Trims
- Parts exposed to solvents or occasional chemical contact