XENOY™ Resin PC PBT T2NX5230
Plastic Granules
XENOY™ Resin T2NX5230 Mineral-filled PC/PET Blend
XENOY™ Resin T2NX5230 is a 16% mineral-filled PC/PET blend with 29 wt% recycled content. It offers high flow, low shrinkage, low CTE, and stable dimensions. Suitable for painted body panels, spoilers, housings, door handles, and EV parts.
Associated Documents
TDS - Europe
Typical property data
Physical Properties
- Density: 1.33 g/cm³ (ISO 1183)
- Melt Flow Rate: 28 g/10 min at 265°C / 5.0 kgf (ASTM D1238)
- Melt Volume Rate: 24 cm³/10 min at 265°C / 5.0 kg (ISO 1133)
- Mold Shrinkage, Flow: 0.5–0.7% on tensile bar (SABIC Method)
- Water Absorption: 0.42% at 23°C / saturated (ISO 62-1)
- Moisture Absorption: 0.14% at 23°C / 50% RH (ISO 62)
Mechanical Properties
- Tensile Stress at Yield: 58 MPa at 5 mm/min (ISO 527)
- Tensile Stress at Break: 42 MPa at 5 mm/min (ISO 527)
- Tensile Strain at Yield: 3.6% at 5 mm/min (ISO 527)
- Tensile Strain at Break: 9% at 5 mm/min (ISO 527)
- Tensile Modulus: 3850 MPa at 1 mm/min (ISO 527)
- Flexural Stress at Yield: 95 MPa at 2 mm/min (ISO 178)
- Flexural Modulus: 3750 MPa at 2 mm/min (ISO 178)
Impact Properties
- Izod Impact, Unnotched at +23°C: 137 kJ/m², specimen 80 × 10 × 4 mm (ISO 180/1U)
- Izod Impact, Unnotched at -30°C: 120 kJ/m², specimen 80 × 10 × 4 mm (ISO 180/1U)
- Izod Impact, Notched at +23°C: 10 kJ/m², specimen 80 × 10 × 4 mm (ISO 180/1A)
- Izod Impact, Notched at -30°C: 7 kJ/m², specimen 80 × 10 × 4 mm (ISO 180/1A)
- Charpy Impact, V-Notch Edgewise at 23°C: 10 kJ/m², specimen 80 × 10 × 4 mm, span 62 mm (ISO 179/1eA)
Thermal Properties
- Coefficient of Thermal Expansion, Flow: 5.4E-05 1/°C from -30°C to 80°C (ISO 11359-2)
- Coefficient of Thermal Expansion, Cross Flow: 7.4E-05 1/°C from -30°C to 80°C (ISO 11359-2)
- Vicat Softening Temperature, Rate B/50: 137°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 140°C (ISO 306)
- Heat Deflection Temperature, HDT/Af: 109°C at 1.8 MPa, flatwise, specimen 80 × 10 × 4 mm, span 64 mm (ISO 75/Af)
Processing Parameters
- Drying Temperature: 110–120°C
- Drying Time: 4–6 hours
- Maximum Moisture Content: 0.02%
- Melt Temperature: 265–275°C
- Nozzle Temperature: 260–275°C
- Front Zone 3 Temperature: 260–280°C
- Middle Zone 2 Temperature: 250–275°C
- Rear Zone 1 Temperature: 240–270°C
- Hopper Temperature: 60–80°C
- Mold Temperature: 60–100°C
Use & Applications
- Body panels, spoilers
- Housings
- Door handles
- Spring-loaded part
- Fuel filler doors
- Medical device enclosures
- EV components